印刷机械用高强双凸轮的热处理工艺研究 被引量:1

Study on Heat Treatment Process of High-strength Double-cam for Printing Machinery
原文传递
导出
摘要 采用等温淬火热处理工艺研制了ADI1000-5球铁双凸轮,其铸态显微组织包含90%的V或VI形状的石墨,并且不含I和II形状的石墨,球化率超过85%,石墨的大小为6级。分析了等温淬火前后双凸轮材料的金相组织。结果表明,经两级淬火后,双凸轮的抗拉强度超过1000 MPa,伸长率达到5%。目前,该双凸轮已研制成功并获得应用。 The ADI1000-5 ductile iron double cam was developed by the isothermal quenching heat treatment process.The cast microstructure has 90%V or VI shaped graphite,and has no I and II shaped graphite,the spheroidizing rate is more than 85%,and the size of the graphite is grade 6.The metallographic microstructure of double cam before and after austempering was analyzed.The results show that the tensile strength of the double cam is more than 1000 MPa and the elongation is 5%after two-stage quenching.At present,the double cam has been successfully developed and applied.
作者 冯苗 张威 王剑 黄引平 FENG Miao;ZHANG Wei;WANG Jian;HUANG Yinping(Center of Technology,Ningxia Tiandi Benniu Yinqi Equipment Co.,Ltd.,Ningxia 750021,China;CSIC No.12 Research Institute,Xingping 713102,China)
出处 《热加工工艺》 北大核心 2020年第2期146-148,共3页 Hot Working Technology
关键词 奥贝球铁 双凸轮 等温淬火 石墨 austempered ductile iron(ADI) double-cam isothermal hardening graphite
  • 相关文献

参考文献3

二级参考文献30

  • 1梁盛文.汽车铸造技术的现状与发展趋势[J].汽车工艺与材料,2007(5):19-25. 被引量:11
  • 2江海涛,唐荻,刘强,刘仁东,严玲.TRIP钢中残余奥氏体及其稳定性的研究[J].钢铁,2007,42(8):60-63. 被引量:48
  • 3Zimba J,Simbi D J,Navara E.Austempered ductile iron:an alternative material for earth moving components[J].Cement & Concret Composites,2003,25:643-649.
  • 4Sidjanin L,Novovie M,Smallman R E.Metallographic investigations of ADI materials[J].Praktische Metallographie,1996,33(1):2-16.
  • 5Voigt R C.Austempered ductile iron-processing and properties[J].Cast Metals,1989,2(2):71-93.
  • 6Kovacs B V.Heat treating of austempered ductile iron[J].AFS Tran,1997,74:501-505.
  • 7Yang J H,Putatunda S K.Influence of a new two-step austempering process on strain-harding behavior of atmtempered ducti|e iron (ADI)[J].Materials Science and Engineering A,2004,382:265-279.
  • 8Yang J H,Putatunda S K.Improvement in strength and toughness of austempered ductile cast iron by a novel two-step austempering process[J].Materials and Design,2004,25:219-230.
  • 9Putatunda S K.Develepment of austempered ductile cast iron with simultaneous high yield strength and fracture toughness by a novel two-step austempering process[J].Materials Science and Engineering A,2001,315:70-80.
  • 10李先芬,余瑾,刘兰俊,刘海明,祖方遒.两步法等温淬火工艺对等温淬火球铁组织和性能的影响[J].材料热处理学报,2008,29(2):82-85. 被引量:9

共引文献19

同被引文献5

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部