稀土氟化镧对多孔铝的性能影响研究 被引量:3

Effect of rare earth lanthanum fluoride on performance of porous aluminum
原文传递
导出
摘要 采用添加造孔剂的方法制备多孔铝试样。研究烧结温度和稀土氟化镧含量对多孔铝材料的性能影响。结果表明,烧结温度为600℃时多孔铝材料的烧结性能最佳;稀土氟化镧的适量加入可以提高多孔铝的力学性能;稀土氟化镧添加量为0.5%时,多孔铝材料的抗压强度和弹性模量最佳,分别为52.4 MPa和1.56 GPa。 Porous aluminum samples were prepared by adding pore forming agent.The effects of sintering temperature and lanthanum fluoride content on the properties of porous aluminum were studied.The results show that the sintering performance of porous aluminum material is the best when the sintering temperature is 600℃,the mechanical properties of porous aluminum can be improved by adding lanthanum fluoride properly,and the compressive strength and elastic modulus of porous aluminum material are the best when the adding amount of lanthanum fluoride is 0.5%,which are 52.4 MPa and 1.56 GPa respectively.
作者 狄玉丽 李霞 肖文 DI Yu-li;LI Xia;XIAO Wen(Xichang University,School of Science,Xichang 615013,China)
机构地区 西昌学院理学院
出处 《粉末冶金工业》 CAS 北大核心 2020年第1期18-22,共5页 Powder Metallurgy Industry
基金 四川省大学生创新创业项目资助(20170628043) 四川省教育厅项目资助(18ZB0543).
关键词 稀土 多孔铝 力学性能 氟化镧 rare earth porous aluminum mechanical property lanthanum fluoride
  • 相关文献

参考文献12

二级参考文献182

共引文献207

同被引文献76

引证文献3

二级引证文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部