AZ91C镁合金表面Ti-TiN复合镀层的阴极多弧离子镀法制备与表征 被引量:4

Ti-TiN Films Prepared by Cathodic Multi Arc Ion Plating on Magnesium Alloy AZ91C
下载PDF
导出
摘要 采用阴极多弧离子镀膜技术,在AZ91C镁合金基底上首次成功镀制了结合力强的以Ti为过渡层的TiN复合膜层,并利用高分辨扫描电子显微镜(SEM)、X射线能谱仪(EDS)、显微划痕测试等技术对复合膜层的形貌、组织结构及性能进行分析研究。结果表明,采用多弧离子镀膜工艺,能在经过恰当预处理的镁合金基底上制备出性能良好的TiN膜,膜层均匀、致密,膜基结合力达130 mN以上,复合硬度达500 HV左右(AZ91镁合金基底为125 HV)。此外中性盐雾强化实验表明,经该方法处理后的镁合金在ASTM-B117标准测试条件下,腐蚀速率明显降低,经过200 h后,表面无明显腐蚀现象。真空多弧离子镀膜技术有望在镁合金表面防护领域得到应用。 TiN films grown on Ti as interlayers were prepared on AZ91C magnesium alloy substrate by cathodic multi arc ion plating.The surface morphology,microstructure and hardness of the films were examined using high-resolution scanning electron microscope(SEM),X-ray energy diffraction spectrometers(EDS) and microcharacter hardness tester.The results show that TiN films with good performance can be obtained on the properly pretreated magnesium substrate by the multi arc ion plating technique.The adhesion force betw...
出处 《腐蚀与防护》 CAS 北大核心 2008年第4期182-184,共3页 Corrosion & Protection
基金 国家支撑计划项目(编号:2006BAE04B05-3) 国家高技术研究发展计划(编号:2006AA05Z411) 教育部长江学者与创新团队发展计划项目(编号:IRT0629) 国家自然基金资助项目(编号:50505037)
关键词 镁合金 阴极多弧离子 TiN复合层 magnesium and alloy cathodic multi arc ion plating TiN film
  • 相关文献

参考文献2

  • 1[1]Ohser-Wiedemann R,Hollstein F.Bayer U[J].Materials Research and Advanced Techniques,2005(96):818-822.
  • 2[2]赵家政,徐洮.分析电子显微使用手册[M].宁夏:宁夏人民教育出版社,1996:100-101.

同被引文献40

  • 1袁琳,高原,张维,王成磊,黄承兴.201不锈钢离子渗氮和离子镀TiN复合强化层的耐蚀性[J].材料热处理学报,2011,32(S1):144-147. 被引量:8
  • 2任志华,彭红瑞.等离子体化学气相沉积TiN涂层刀具的应用研究[J].青岛化工学院学报(自然科学版),1995,16(4):345-349. 被引量:7
  • 3史新伟,李杏瑞,邱万起,刘正义.电弧离子镀TiN及其复合膜的腐蚀机理探讨[J].真空科学与技术学报,2006,26(4):330-334. 被引量:14
  • 4姜雪峰,刘清才,王海波.多弧离子镀技术及其应用[J].重庆大学学报(自然科学版),2006,29(10):55-57. 被引量:47
  • 5AMBAT R, ZHOU W. Electroless nickel-plating on AZ91D magnesium alloy: effect of substrate microstructure and plating parameters [J]. Surface and Coatings Technology, 2004, 179 (2/3): 124-134.
  • 6GRAY J E, LUAN B. Protective coatings on magnesium and its alloys--a critical review [J]. Journal of AUoys and Compounds, 2002, 336 (1/2): 88-113.
  • 7BAKKAR A, NEUBERT V. Electrodeposition onto magnesium in air and water stable ionic liquids: From corrosion to successful plating [J]. Electrochemistry Communications, 2007, 9 (9): 2428-2435.
  • 8ZHANG J F, YAN C W, WANG F H. Electrodeposition of AI-Mn alloy on AZ31B magnesium alloy in molten salts [J]. Applied Surface Science, 2009, 255 (9): 4926-4932.
  • 9NORDLIEN J H, ONO S, MASUKO N, et al. A TEM investigation of naturally formed oxide films on pure magnesium [J]. Corrosion Science, 1997, 39 (8): 1397-1414.
  • 10YANG L H, LI J Q, ZHENG Y Z, et al. Electroless Ni-P plating with molybdate pretreatment on Mg-8Li alloy [J]. Journal of Alloys and Compounds, 2009, 467 (1/2): 562-566.

引证文献4

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部