摘要
The Ti-doped waveguide-type periodically poled LiNbO3 (PPLN) were fabricated and the dependence of domain wall velocity on an external field applied for domain inversion was investigated. The whole polarization reversal process was computer-controlled to regulate domain wall expansion at a feedback time shorter than 5 μs. The coercive voltage and several values of excess voltage were applied on 500 μm-thick wafers serially connected to a 1-MOhm external resistor which had an effect of the poling current reduction, i.e. the deceleration of domain wall expansion. The domain wall velocity is sensitive to the poling voltage, precisely speaking, to the excess voltage. The domain wall velocities were 28.70, 16.02 and 5.75 μm·s-1 under poling field of 23.5, 22.0 and 21.0 kV·mm-1, respectively. Moreover, average duty cycle of PPLN is about 49.93%.