Effects of casting speed on microstructure and segregation of electromagnetically stirred Aluminum alloy in continuous casting process 被引量:2

Effects of casting speed on microstructure and segregation of electromagnetically stirred Aluminum alloy in continuous casting process
下载PDF
导出
摘要 Recently, a semi-solid metal processing has been acknowledged as a cost-effective technique to be able to manufacture high quality product for the transportation industry. In this study a hypo-eutectic Al alloy was fabricated by means of an electromagnetic stirrer in continuous casting process and the microstructural change during solidification due to a fluid flow by electromagnetic stirring was examined. Due to the forced fluid flow during solidification a dendritic phase of primary α phase of Al alloy was turned into a globular phase, which can make the Al alloy get a thixotropic behavior in the semi-solid region. In order to establish the quantitative relationship between microstructure and the process parameters, the morphology shape, a silicon distribution and a size of primary α phase were observed according to casting speed in continuous casting machine. The primary α phase was turned into the degenerate dendrites approaching a spherical configuration with increasing casting speed. The fine-grained and equiaxed microstructure appeared at higher casting speed. A segregation behavior of Si element was declined with increasing casting speed and a very uniform distribution of Si element was observed on the billet at a casting speed of 600 mm·min-1. A thickness of the solidifying shell of the billet was shortened with increasing the casting speed. Recently, a semi-solid metal processing has been acknowledged as a cost-effective technique to be able to manufacture high quality product for the transportation industry. In this study a hypo-eutectic Al alloy was fabricated by means of an electromagnetic stirrer in continuous casting process and the microstructural change during solidification due to a fluid flow by electromagnetic stirring was examined. Due to the forced fluid flow during solidification a dendritic phase of primary α phase of Al alloy was turned into a globular phase, which can make the Al alloy get a thixotropic behavior in the semi-solid region. In order to establish the quantitative relationship between microstructure and the process parameters, the morphology shape, a silicon distribution and a size of primary α phase were observed according to casting speed in continuous casting machine. The primary α phase was turned into the degenerate dendrites approaching a spherical configuration with increasing casting speed. The fine-grained and equiaxed microstructure appeared at higher casting speed. A segregation behavior of Si element was declined with increasing casting speed and a very uniform distribution of Si element was observed on the billet at a casting speed of 600 mm·min-1. A thickness of the solidifying shell of the billet was shortened with increasing the casting speed.
出处 《Rare Metals》 SCIE EI CAS CSCD 2006年第z2期118-123,共6页 稀有金属(英文版)
基金 This work was financiallysupported bythe KISTProgram(No.2E19470)and by the Components&Materials Technology Development Program of Ministry of Commerce,Industry and Energy of Korea.
关键词 semi-solid slurry electromagnetic stirring casting speed SEGREGATION Al alloy semi-solid slurry electromagnetic stirring casting speed segregation Al alloy
  • 相关文献

参考文献2

二级参考文献4

  • 1毛卫民.北京科技大学博士学位论文[M].,1999..
  • 2毛卫民,博士学位论文,1999年
  • 3Doherty R D,Mater Sci Eng,1984年,65卷,181页
  • 4潘冶金,张春燕.半固态铝合金及粒状晶的形成[J].铸造工程.造型材料,1999,23(3):28-30. 被引量:2

共引文献55

同被引文献10

引证文献2

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部