一种常温三价铬镀锌黑钝化方法 被引量:1

A Method of Darkening Passivation for Galvanization Used Chromium(Ⅲ) at Room Temperature
下载PDF
导出
摘要 以磷酸铬为主要成膜物,有机羧酸为络合剂,通过添加作为发黑剂的镍钴盐,和一定量的硝酸根、氟化钠和二氧化硅的水溶胶,制备出了镀锌黑钝化常温发黑液,其中性盐雾试验可分别达到挂镀56 h,滚镀48 h,红锈出现时间为120 h和92 h。 Chromium(III) phosphate used as primary film forming material,carboxylic acid as complexing agent,inorganic nickel and cobalt compounds as darkening agent,added quantitative nitrate,sodium fluoride and silicon dioxide hydrosol,the blacking passivation solution for galvanization at room temperature was prepared.The neutral salt spary test were respectively 56 h for hang plating and 48 h for barrel plating.The red rust appeared respectively at 120 h and 92 h.
出处 《广东微量元素科学》 CAS 2008年第6期67-69,共3页 Trace Elements Science
关键词 三价铬 镀锌 常温钝化 成膜物 chromium(III) galvanization passivation at room temperature film forming
  • 相关文献

参考文献6

二级参考文献16

  • 1胡立新,兰林,朱中兵,欧阳贵.镀锌层三价铬高耐蚀蓝白钝化工艺研究[J].材料保护,2005,38(7):25-27. 被引量:16
  • 2方明.镀锌黑钝化工艺[J].表面技术,1996,25(4):49-52. 被引量:7
  • 3李秀英.三价铬钝化在生产中的应用[J].电镀与环保,2006,26(3):42-43. 被引量:19
  • 4孙文军.镀锌黑钝化[J].电镀与环保,1997,17(1):36-36.
  • 5施镇涛.镀锌用三价铬蓝白色钝化剂及其制造方法:中国,1 594 651[P].2005,03-16.
  • 6陈笃慧 陈声培 叶世源.锌黑色钝化膜的组成及其形成机理.厦门大学学报:自然科学版,1987,26(4):456-461.
  • 7Bayati M R,Shariat M H,Janghorban K.Design of Chemical Composition and Optimum Working Conditions for Trivalent Black Chromium Electroplating Bath Used for Solar Thermal Collectors[J].Renewable Energy,2005,30(14):2163-2178.
  • 8Zaki Nabil.Tfivalent Chrome Conversion Coating for ZinC and Zinc Alloys[J].Metal Finishing,2002,100(Supplemental 1):492-501.
  • 9屠振密,张景双,于元春,等.无铬钝化与三价铬钝化的研究进展:表面工程技术创新研讨会论文集[C].贵阳:[出版者不详],2005:37-41.
  • 10Zaki Nabil.Producing Cr (Ⅵ)-free Black Finishing for Automotive Applications:AESF SUR/FIN 2004 & Interfinish 2004 World Congress[C].Chicago,Minois,2004:494.

共引文献22

同被引文献27

  • 1肖鑫,钟萍,易翔.一种新型镀锌层无铬钝化工艺[J].腐蚀与防护,2007,28(9):467-469. 被引量:5
  • 2沈品华.镀锌三价铬钝化[J].电镀与环保,2007,27(3):27-30. 被引量:12
  • 3任艳萍,陈锦虹.镀锌层三价铬钝化工艺的研究[J].腐蚀与防护,2007,28(1):13-16. 被引量:8
  • 4毕四富,李宁,屠振密,王亚伟.镀锌层三价铬黑色钝化工艺的研究[J].电镀与环保,2007,27(4):17-20. 被引量:8
  • 5Camila Boin. Black passivation films without hexava- lent chromium on top of electroplated layers of zinc and zinc alloys[C]//SAE Brasil 2007 Congress and Exhib- it, Sao Paulo, Brazil, 2007 : 2593--2600.
  • 6Ernest John Wilhelm, Palmerton Pa. Method of coat- ing zinc or cadmium base metals [P]. US Pat: 2035380,1936-03-24.
  • 7Nabil Z. Trivalent chromate conversion coating for zinc and zinc alloys[C]//Metal Finishing Guidebook Directory, New York, 2002 : 492--501.
  • 8Huvar. Trivalent chromium passivation solution and process[P]. US Pat:4349392,1982-09-14.
  • 9Tang, Bhatia, Parkos, et al. Stability additive for triva- lent chrome conversion coating bath solution[P]. US Pat.. 6648986,2003-11-18.
  • 10Matzdorf,Kane,Green. Post-treatment for metal coa- ted substrates[P]. US Pat: 6527841,2003-03-04.

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部