XPS analyses have been performed to investigate the chemical conditions of Ni and oxygen on grain surfaces in single-sintered SrTiO3 capacitor-varistor ceramic doped with Nb2O5 and NiO. It is ascertained that Ni is in form of Ni2+ ions, which substitute for Ti4+ ions on grain surfaces during the oxidizing annealing. Moreover, it is confirmed that three kinds of chemically adsorbed oxygen such as O2-, O- and O-2(-) are formed on grain surfaces. It is proposed that these behaviors contribute greatly to the generation of multiple types of grain boundary acceptor states in the ceramic.
XPS analyses have been performed to investigate the chemical conditions of Ni and oxygen on grain surfaces in single-sintered SrTiO3 capacitor-varistor ceramic doped with Nb2O5 and NiO. It is ascertained that Ni is in form of Ni2+ ions, which substitute for Ti4+ ions on grain surfaces during the oxidizing annealing. Moreover, it is confirmed that three kinds of chemically adsorbed oxygen such as O2-, O- and O-2(-) are formed on grain surfaces. It is proposed that these behaviors contribute greatly to the generation of multiple types of grain boundary acceptor states in the ceramic.