摘要
The correlation between the effective magnetic anisotropy 〈κ〉 and the temperature T, 〈κ〉-T curve, for the Fe83Nb6B11 alloys as-cast and annealed at 460-580°C was investigated. The experimental results of the 〈κ〉-T curves for nanocrystalline samples were explained using the theory of exchange interaction between α-Fe grains.
The correlation between the effective magnetic anisotropy 〈κ〉 and the temperature T, 〈κ〉-T curve, for the Fe83Nb6B11 alloys as-cast and annealed at 460-580°C was investigated. The experimental results of the 〈κ〉-T curves for nanocrystalline samples were explained using the theory of exchange interaction between α-Fe grains.
作者
Y.J. Zhang1), Z. Wang1,2), K. Y. He1), H.H. Zhao1), L.Z. Cheng1) and H.C. Yang1) 1) Department of Materials Science and Engineering, Northeastern University, Shenyang 110004, China 2) Tianjin Institute of Technology, Tianjin 300191,
基金
the National Natural Science Foundation of China (Grant No.59871013).