自修复剂摩擦学性能研究的试验方法探讨 被引量:2

Discussion on Test Methods for the Tribological Performance of Self-Repairing Lubricating Oil Additives
下载PDF
导出
摘要 采用四球摩擦磨损试验机考察了三种自修复剂:SJS、SSY和SKD的减摩抗磨以及自修复性能,并与未加自修复剂的SJ10W-40汽油机油作对比,同时探讨了四球机试验法对自修复剂性能评价的适用性。试验完成后,分别利用三维白光干涉表面形貌仪、扫描电子显微镜(SEM)以及EDS能谱仪,对小球磨斑的粗糙度、表面形貌以及表面元素进行了分析。结果表明:自修复剂的加入使得油样的摩擦系数减小,说明自修复剂具有一定的减摩抗磨作用。表面分析研究表明,在采用四球机试验方法获得的磨斑表面上,自修复剂并未体现自修复效果,说明四球机试验法(SH/T 0189)不适用于SJS、SSY和SKD自修复剂自修复性能的评价。 The tribological properties of self-repairing lubricating oil additives(SJS,SSY and SKD)were studied by using a MS-10J 4-Balls Machine.A comparison was made between the base oil(SJ 10W-40) and the oil(SJ 10W-40) with the three addictives.The applicability of the 4-Ball test method that evaluates the self-repairing property of the additives was discussed.The roughness,surface morphologies and elementary composition of wear spot of the balls were analyzed by using Phase Shift Micro XAM-3D,SEM(FEI Quanta 200) ...
出处 《润滑油》 CAS 2011年第2期44-48,共5页 Lubricating Oil
关键词 油膜 减摩抗磨 自修复 竞争吸附性 oil film friction-reducing and antiwear self-repairing competitive adsorption
  • 相关文献

参考文献5

二级参考文献51

共引文献53

同被引文献16

引证文献2

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部