Wear Properties of Plasma Nitrided H13 Steel at Room and Elevated Temperature 被引量:2

Wear Properties of Plasma Nitrided H13 Steel at Room and Elevated Temperature
原文传递
导出
摘要 H13 steel was nitrided using a plasma surface alloying technique at the temperature of 570℃.The nitrided layers with different thicknesses and components were obtained by changing nitriding pressure.The microstructure and composition of the nitrided layers were evaluated by optical microscopy(OM)and X-ray diffraction(XRD).The wear properties of the nitrided layer against Al2O3 ball at room temperature using a ball-on-disc tribometer and against Si3N4 ball at elevated temperature using a HT-2001 abrasive wear test machine were investigated.The results show that the nitrided layers are composed of compound layer and diffusion layer at the pressure of 100 and 450 Pa.No obvious compound layer appears at pressure of 200 and 300 Pa.XRD analysis shows the nitrided layers are mainly composed ofε-Fe2-3N,γ'-Fe4N,α-Fe,Fe2O3 and Fe3O4 phases.The surface hardness of plasma nitrided H13 steel is about 1100HV0.050 doubled that of substrate.The room temperature friction coefficient of H13 steel is reduced and wear rate is decreased by nitriding at 200 and 300 Pa.Elevated temperature wear test indicates the nitrided H13 steel at the pressure of 100 Pa shows lower friction coefficient and wear rate which are reduced more than 6 times compared with that of H13 substrate. H13 steel was nitrided using a plasma surface alloying technique at the temperature of 570℃.The nitrided layers with different thicknesses and components were obtained by changing nitriding pressure.The microstructure and composition of the nitrided layers were evaluated by optical microscopy(OM)and X-ray diffraction(XRD).The wear properties of the nitrided layer against Al2O3 ball at room temperature using a ball-on-disc tribometer and against Si3N4 ball at elevated temperature using a HT-2001 abrasive wear test machine were investigated.The results show that the nitrided layers are composed of compound layer and diffusion layer at the pressure of 100 and 450 Pa.No obvious compound layer appears at pressure of 200 and 300 Pa.XRD analysis shows the nitrided layers are mainly composed ofε-Fe2-3N,γ’-Fe4N,α-Fe,Fe2O3 and Fe3O4 phases.The surface hardness of plasma nitrided H13 steel is about 1100HV0.050 doubled that of substrate.The room temperature friction coefficient of H13 steel is reduced and wear rate is decreased by nitriding at 200 and 300 Pa.Elevated temperature wear test indicates the nitrided H13 steel at the pressure of 100 Pa shows lower friction coefficient and wear rate which are reduced more than 6 times compared with that of H13 substrate.
出处 《稀有金属材料与工程》 SCIE EI CAS CSCD 北大核心 2012年第S1期203-206,共4页 Rare Metal Materials and Engineering
基金 National Natural Science Foundation of China(50771070) Scientific and Technological Development Project of Shanxi Province,China(20100321078-02) High Technology and Key Development Project of Ningbo,China(2009B10010)
关键词 plasma NITRIDING H13 steel ELEVATED temperature WEAR plasma nitriding H13 steel elevated temperature wear
  • 相关文献

参考文献14

  • 1ZHANG Mi-lan,XING Shu-ming,XIN Qiao,XIAO Li-ming,GOU Jun-nian,WU Xia-ling.Abnormal Failure Analysis of H13 Punches in Steel Squeeze Casting Process[J].Journal of Iron and Steel Research International,2008,15(3):47-51. 被引量:13
  • 2Norstrom L A,Svensson M,Ohrberg N.Thermal-Fatigue Behaviour of Hot-Work Tool Steels. Metals Technology . 1981
  • 3Sandberg O,Klarenfjord B,and Miller P.Properties profile:comparison of premium quality H13&modified hot work die steel. Casting Engineer Die . 2002
  • 4Guobin Li,Xiangzhi Li,Jianjun Wu.Study of the thermal fatigue crack initial life of H13 and H21 steels. Journal of Materials . 1998
  • 5MIN Yong-an WU Xiao-chun WANG Rong LI Lin XU Luo-ping.Prediction and Analysis on Oxidation of H13 Hot Work Steel[J].Journal of Iron and Steel Research International,2006,13(1):44-49. 被引量:7
  • 6M Kchaou,R Elleuch,Y Desplanques,X Boidin,G Degallaix.Failure mechanisms of H13 die on relation to the forging process—a case study of brass gas valves. Eng Fail Anal . 2010
  • 7Zhou Q G,Bai X D,Chen X W,et al.Corrosion resistance of duplex and gradient CrNx coated H13 steel. Applied Surface Science . 2003
  • 8Leite M V,Figuero C A,Corujeira Gallo S et al. Wear . 2010
  • 9Torres Ricardo D,Soares Paulo C Jr,Schmitza Cleomar et al. Surface and Coatings Technology . 2010
  • 10Okorafor O E. Journal of Materials Science . 1987

二级参考文献22

  • 1R. Lapovok,S. Smirnov,V. Shveykin.Damage mechanics for the fracture prediction of metal forming tools[J].International Journal of Fracture.2000(2)
  • 2Ghomashchi M R,Vikhrov A.Squeeze Casting :an Overview[].Journal of Materials.2000
  • 3Lapovok R,Smirnov S,Shveykin V.Damage Mechanics for the Fracture Prediction of Metal Forming Tools[].International Journal of Fracture.2000
  • 4Ki m D H,Lee HC,Ki mB M,et al.Esti mation of Die Service Life Against Plastic Deformation and Wear During Hot Forging Processes[].Journal of Materials.2005
  • 5LI Ke-min,WEN Zhi-gao.Failure Models and Ways of I mpro- ving Life of H13 Male Punchin Hot Extrusion[].Metal Forming.2003
  • 6ZHAO Chang-sheng,JUJian-cun.Failure Analyzing of H13 Steel in Hot Extrusion Die[].Metal Forming.2002
  • 7Shida S.Empirical Formula of FlowStress of Carbon Steels-Re- sistance to Deformation of Carbon Steels at Elevated Tempera- ture[].Journal of the Japan Society for Technology of Plasticity.1969
  • 8Suzuki H,Hashizume S,Yabuki Y,et al.Studies on the Flow Stress of Metals and Alloys[].Report of the Institute of In- dustrial Science.1968
  • 9Rusinek A,Klepaczko J R.Shear Testing of a Sheet Steel at Wide Range of Strain Rates and a Constitutive Relation With Strain-Rate and Temperature Dependence of the Flow Stress[].International Journal of Plasticity.2001
  • 10Lee Y,Ki m B M,Park K L,et al.AStudy for the Constitu- tive Equation of Carbon Steel Subjectedto Large Strains , High Temperature and High Strain Rates[].Journal of Materials.2002

共引文献18

同被引文献9

引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部