Pore Structure of Cement Pastes Mixed with Inorganic Salts

Pore Structure of Cement Pastes Mixed with Inorganic Salts
原文传递
导出
摘要 The influence of salts on concrete durability,pore structure of cement pastes with inorganic salts,including CaCl2,NaCl,Na2SO4,NaNO2,Ca(NO3)2 and Ca(NO2)2,was studied through mercury intrusion porosimetry (MIP),and hydration degree of each paste was also tested.The results show that porosity of the paste with inorganic salt cured for 3 d or 28 d was related with its hydration degree.For the pore size distribution,the pores smaller than 50 nm in paste with salts cured for 3 d increased;the amount of pores larger than 100 nm increased because of the addition of Ca (NO3)2 at 3 d,but these coarse pores turned into fine pores and reduced significantly at 28 d;coarse pores lager than 1000 nm in cement pastes containing NaCl and Na2SO4 increased. The influence of salts on concrete durability,pore structure of cement pastes with inorganic salts,including CaCl2,NaCl,Na2SO4,NaNO2,Ca(NO3)2 and Ca(NO2)2,was studied through mercury intrusion porosimetry (MIP),and hydration degree of each paste was also tested.The results show that porosity of the paste with inorganic salt cured for 3 d or 28 d was related with its hydration degree.For the pore size distribution,the pores smaller than 50 nm in paste with salts cured for 3 d increased;the amount of pores larger than 100 nm increased because of the addition of Ca (NO3)2 at 3 d,but these coarse pores turned into fine pores and reduced significantly at 28 d;coarse pores lager than 1000 nm in cement pastes containing NaCl and Na2SO4 increased.
作者 杨文萃
出处 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2009年第S1期210-213,共4页 武汉理工大学学报(材料科学英文版)
关键词 inorganic salts pore structure mercury intrusion porosimetry inorganic salts pore structure mercury intrusion porosimetry
  • 相关文献

参考文献1

二级参考文献12

共引文献17

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部