The catalyst {[(2-ArN=C(Me))2C5H3N]FeCl3} (Ar = 2-C6H4(i-Pr)) with methylaluminoxane (MAO) as co-catalyst was intercalated between layers of montmorillonite (MMT) for ethylene oligomerization. Metallocene catalyst Me2Si(Ind)2ZrCl2 and MAO was then added to form a dual functional catalytic system. A PE/MMT nanocomposite was prepared by copolymerization of ethylene with α-olefins produced in situ from ethylene over the dual functional catalytic system. The catalytic system was of high polymeric activity. The resultant PE/MMT nanocomposites were stable and got increases in tensile strength and temperature of maximum weight loss (Tonset).
The catalyst [(2-ArN=C(Me))2C5H3N]FeCl2 (Ar = 2-C6H4(i-Pr)) with methylaluminoxane (MAO) as cocatalyst was intercalated between layers of montmorillonite (MMT) for ethylene oligomerization. Metallocene catalyst Me2Si(Ind)2ZrCl2 and MAO was then added to form a dual functional catalytic system. A PE/MMT nanocomposite was prepared by copolymerization of ethylene with α-olefins produced in situ from ethylene over the dual functional catalytic system. The catalytic system was of high polymeric activity. The resultant PE/MMT nanocomposites were stable and got increases in tensile strength and temperature of maximum weight loss (Tonset).
基金
This work was supported by the National Natural Science Foundation of China (Grant Nos. 29734141 and 50103012).