The free-cutting phase in RE or Ca-RE treated sulfur-containing free-cutting steel is the eutectic phases of MnS-RE_2S_3 and (Mn,Ca)S-RE_2S_3,respectively.The atomic ratio of RE/S needed to modify all the MnS into the eutectic phase is higher than 1.48 or 1.41-1.37 Ca/S,when RE or Ca-RE is used as the modifiz- er in the sulfur-containing free-cutting steel.Moreover,the thermodynamical calculation shows that the eutectic temperature is lower than the solidifying temperature,which is the key condition for the eutectic phase to keep globual during solidifying.
The free-cutting phase in RE or Ca-RE treated sulfur-containing free-cutting steel is the eutectic phases of MnS-RE_2S_3 and (Mn,Ca)S-RE_2S_3,respectively.The atomic ratio of RE/S needed to modify all the MnS into the eutectic phase is higher than 1.48 or 1.41-1.37 Ca/S,when RE or Ca-RE is used as the modifiz- er in the sulfur-containing free-cutting steel.Moreover,the thermodynamical calculation shows that the eutectic temperature is lower than the solidifying temperature,which is the key condition for the eutectic phase to keep globual during solidifying.
基金
The project supported by the National Natural Science Foundation of China