Solid Solubility and Age Hardening of Rapidly Solidified Al-Er Alloys

Solid Solubility and Age Hardening of Rapidly Solidified Al-Er Alloys
下载PDF
导出
摘要 The metastable extension of solid solubility and age hardening of rapidly solidified Al-Er alloy were inves- tigated.The splat foils(0.04~0.06 mm in thickness)and spun ribbons(0.02~0.04 mm in thickness)of Al-Er alloys were prepared by melt hammer-anvil and melt spinning techniques,respectively.The cooling rate was about 10~6~10~7 K/s.The metastable extended solid solubility of Er in Al evaluated by measurements of lat- tice parameters of rapidly solidified alloys was 0.75 at%.An age hardening response was observed in the quenched and aged specimen.The precipitate responsible for age hardening was identified to be Cu_3Au type cubic Al_3Er. The metastable extension of solid solubility and age hardening of rapidly solidified Al-Er alloy were inves- tigated.The splat foils(0.04~0.06 mm in thickness)and spun ribbons(0.02~0.04 mm in thickness)of Al-Er alloys were prepared by melt hammer-anvil and melt spinning techniques,respectively.The cooling rate was about 10~6~10~7 K/s.The metastable extended solid solubility of Er in Al evaluated by measurements of lat- tice parameters of rapidly solidified alloys was 0.75 at%.An age hardening response was observed in the quenched and aged specimen.The precipitate responsible for age hardening was identified to be Cu_3Au type cubic Al_3Er.
作者 宁远涛 戴红
出处 《Rare Metals》 SCIE EI CAS CSCD 1992年第3期202-206,共5页 稀有金属(英文版)
基金 The project was supported by National Natural Science Foundation of China(5870071).
关键词 Al-Er alloys Solid solubility Age hardening Rapid solidification Al_3Er Al-Er alloys Solid solubility Age hardening Rapid solidification Al_3Er
  • 相关文献

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部