Based on the thermodynamic calculation, the mole ratio of CaO to SiO 2, temperature and A/S of bauxite have a profound influence on the mole ratio of 2CaO·SiO 2 to CaO·SiO 2 in sinter. CaO·SiO 2 and β -2CaO·SiO 2 appear stable in caustic solution but unstable in soda solution, and CaO·SiO 2 is more stable than β -2CaO·SiO 2 under the same leaching condition. Compared with the conventional sinter, the rate of alumina extraction of the new sinter is large and the secondary reaction is restricted in the leaching, which might be mainly due to the more content of CaO·SiO 2 in sinter and better stability of CaO·SiO 2 in leaching.
Based on the thermodynamic calculation, the mole ratio of CaO to SiO 2, temperature and A/S of bauxite have a profound influence on the mole ratio of 2CaO·SiO 2 to CaO·SiO 2 in sinter. CaO·SiO 2 and β -2CaO·SiO 2 appear stable in caustic solution but unstable in soda solution, and CaO·SiO 2 is more stable than β -2CaO·SiO 2 under the same leaching condition. Compared with the conventional sinter, the rate of alumina extraction of the new sinter is large and the secondary reaction is restricted in the leaching, which might be mainly due to the more content of CaO·SiO 2 in sinter and better stability of CaO·SiO 2 in leaching.
出处
《中国有色金属学会会刊：英文版》
CSCD
2003年第1期213-216,共4页
Transactions of Nonferrous Metals Society of China
基金
Project(G19990 6 4910)supportedbytheStateKeyFundamentalResearchProgramofChina
Project( 5 0 2 740 76)supportedbytheNa tionalNaturalScienceFoundationofChina