水热法α-Al_2O_3自发结晶和形态控制 被引量:6

Morphological Forms Control of α-Al_2O_3 Crystal Spontaneously Synthesized by Hydrothermal Method
下载PDF
导出
摘要 本文研究了高温高压水热法合成α Al2 O3 晶体的形态特征。在水热条件下 ,α Al2 O3 的晶体形态和合成温度、矿化剂浓度有密切关系。当KOH浓度和温度较低时 (如 0 .1MKOH ,390℃ ) ,显露c{ 0 0 0 1}、a{ 11 2 0 }、r{ 0 1 12 }、n{ 11 2 3}晶面。随着矿化剂浓度和温度的提高 ,晶体r{ 0 1 12 }和n{ 11 2 3}面的显露面积越来越小 ,直到完全消失 (如2MKOH ,4 0 0℃ ) ,晶体只显露底面c{ 0 0 0 1}、和柱面a{ 11 2 0 } 。 The shape and the interface morphological forms of α-Al_2O_3 crystal synthesized by hydrothermal method at high temperature and high pressure were investigated. Under the hydrothermal conditions, the shapes of the α-Al_2O_3 crystal have a close correlation with synthesized temperature and mineralizer concentration.When the concentration of KOH and the temperature are rather low (eg.0.1M KOH,390℃),the exposed faces of crystal are faces c{0001},a {11-20},r{01-12},n{11-23}. With the increase of the mineralizer concentration and the temperature, the exposed areas of faces r{01-12} and n{11-23} become smaller and smaller, till disappeared(eg. 2M KOH, 400℃), then the crystal only exposes bottom faces c {0001} and prism faces a {11-20}, and appears hexagonal prism.
出处 《人工晶体学报》 EI CAS CSCD 北大核心 2004年第3期380-383,共4页 Journal of Synthetic Crystals
基金 河北省自然科学基金 ( 5 0 2 12 3 ) 河北省科技攻关 ( 2 2 12 2 0 4) 河北省教育厅资助项目 ( 2 0 0 2 15 8)
关键词 水热法 Α-AL2O3 水热合成工艺 晶体 水热反应 矿化剂 生长速度 Al_2O_3 hydrothermal synthesis crystal morphological forms
  • 相关文献

参考文献14

  • 1[1]Hartman P, et al. The Attachment Energy as Habit Controlling Factor[J]. J. Crystal growth, 1980, 49:166.
  • 2[2]Hartman P, et al. The Effect of Surface Relaxation on Crystal Habit: Cases of Corundum (α-Al2O3) and Hematite (α-Fe2O3)[J]. J. Crystal growth,1989, 96:667.
  • 3[3]Watanabe K, et al. Effects of Trivalent Rare-earth Ions upon the Morphology of Corundum Crystals[J]. J. Crystal growth,1983, 65:568.
  • 4[4]Mackrodt W C, et al. The Morphology of α-Al2O3 and α-Fi2O3:the Importance of Surface Relaxation[J]. J. Crystal Growth., 1987,80:441.
  • 5王步国,田明原,施尔畏,仲维卓,郭景坤.水热条件下直接制备的α-Al_2O_3微晶的形态特征[J].科学通报,1997,42(24):2663-2667. 被引量:22
  • 6田明原,施尔畏,元如林,王步国,李汶军,仲维卓,庄击勇.铝氢氧化物和氧化物晶粒的热液法制备及其形成机理[J].中国科学(E辑),1998,28(2):113-118. 被引量:26
  • 7李汶军,郑燕青,施尔畏,陈之战,殷之文.TiO_2和α-Al_2O_3晶体的生长习性[J].无机材料学报,2000,15(6):968-976. 被引量:23
  • 8[8]Li W J, et al. Growth Habit of Rutile and α-Al2O3 Crystals[J]. J. Crystal Growth, 2000,208:546-554.
  • 9[9]Cho S B, Venigalla S, Adair J H. Morphological Forms of α-Alurina Particles Synthesized in 1.4-Butanediol Solution[J]. J. Am. Ceram. Soc., 1996,79(1) :88-96.
  • 10[10]Bell N S, Cho S B, Adair J H. Size Control of α-Alumina Particles Synthesized in 1.4-Butanediol Solutionbyα-Alumina and α-Hematite[J].J.Am. Ceram. Soc.,1998,81(6):1411-20.

二级参考文献23

  • 1仲维卓,刘光照,施尔畏,华素坤,唐鼎元,赵庆兰.在热液条件下晶体的生长基元与晶体形成机理[J].中国科学(B辑),1994,24(4):349-355. 被引量:62
  • 2仲维卓,J Cryst Growth,1996年,166卷,91页
  • 3施尔畏,中国科学.E,1998年,28卷,1期,37页
  • 4Inoue M,Tanino H,kondo Y,Inui T.Formation of Microcrystlline α-Alumina by Glycothermal Treatment of Gibbsite.J.Am.Ceram.Soc.,1989,72(2):352-35
  • 5Cho S B,Venigalla S,Adair J H.Morphological Forms of α-Alumina particles Synthesized in 1.4-Butanediol Solution.J.Am.Ceram.Soc.,1996,79(1):88-96
  • 6Bell N S,Cho S B,Adair J H.Size Control of α-Alumina Particles Synthesized in 1.4-Butanediol Solution by α-Alumina and α-Hematite Seeding.J.Am.Ceram.Soc.,1998,81(6):1411-20
  • 7Sharma P K M,Jilav H,Burgard D,Nass R,Schmidt H.Hydrothermal Synthesis of Nanosize α-Al2O3 from Seeded Aluminum Hydroxide.J.Am.Ceram.Soc.,1998,81(10):2732-34
  • 8Li Wen-jun,Shi Er-wei,Yin Zhi-wen.Growth Habit of Rutile and α-Al2O3 Crystals.J.Crystal Growth,2000,208:546-554
  • 9王步国,施尔畏,仲维卓,殷之文.水热法制备的氧化锌微晶的形态特征[J].科学通报,1997,42(10):1113-1117. 被引量:19
  • 10王步国,田明原,施尔畏,仲维卓,郭景坤.水热条件下直接制备的α-Al_2O_3微晶的形态特征[J].科学通报,1997,42(24):2663-2667. 被引量:22

共引文献68

同被引文献142

引证文献6

二级引证文献15

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部