The new room-temperature molten salt was prepared based on LiTFSI[LiNC(SO 2CF 3) 2] with OZO(C 3H 5NO 2) which were not reported in literature. Its thermal and electrochemical properties were studied by differential scanning calorimetry, ac impedance spectroscopy and cyclic voltammertry respectively. The results indicated that the structure symmetry of the molecule was depressed and the extent of charges delocalization was expanded, because of introducing oxygen atom of differential electronegativity in OZO molecule. DSC analysis showed that the LiTFSI-OZO molten salt has the excellent thermal stability and its eutectic temperature is below about 223.15 K. Meanwhile, the conductivity of LiTFSI-OZO molten salt at a molar ratio of 1∶4.5 is 0.75×10 -3 S/cm at 298.15 K and 3.50×10 -3 S/cm at 333.15 K. CV analysis showed that the electrochemical window of the sample is about 4 V.
The new room-temperature molten salt was prepared based on LiTFSI[LiNC(SO 2CF 3) 2] with OZO(C 3H 5NO 2) which were not reported in literature. Its thermal and electrochemical properties were studied by differential scanning calorimetry, ac impedance spectroscopy and cyclic voltammertry respectively. The results indicated that the structure symmetry of the molecule was depressed and the extent of charges delocalization was expanded, because of introducing oxygen atom of differential electronegativity in OZO molecule. DSC analysis showed that the LiTFSI-OZO molten salt has the excellent thermal stability and its eutectic temperature is below about 223.15 K. Meanwhile, the conductivity of LiTFSI-OZO molten salt at a molar ratio of 1∶4.5 is 0.75×10 -3 S/cm at 298.15 K and 3.50×10 -3 S/cm at 333.15 K. CV analysis showed that the electrochemical window of the sample is about 4 V.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2004年第11期2116-2118,共3页
Chemical Journal of Chinese Universities
基金
国家重点基础研究发展计划(批准号:2002CB211800)
国家基础研究重大项目前期研究专项基金(批准号:2001CCA05000)资助.