摘要
The methyl methacrylate(MMA) reversible addition-fragmentation chain transfer(RAFT) miniemulsion polymerization in the presence of β-cyclodextrin(β-CD) was investigated. β-CD is found to act both as an efficient solubilizer for RAFT agent(2-cyanopro-2-yl dithiobenzoate) and as a stabilizer for heterogeneous polymerization. The RAFT miniemulsion polymerizations with or without β-CD were compared in terms of kinetics and the molecular weight distribution. The problem of poor latex stability was observed in this system. A good result of the control over RAFT miniemulsion polymerization of MMA was obtained with β-CD. The increase of the molecular weight of poly(methyl methacrylate) shows a linear relationship with the monomer conversion. The polydispersity index of the polymer with β-CD(PDI=1.18—1.21) is smaller than that without β-CD. TEM photographs showed that the PMMA particles produced with β-CD had smooth surfaces and uniform particle size. Higher amount of sodium dodecyl sulfate and hexadecane was found in favor of improving the controllability of the system. Oil soluble initiator is beneficial to the controllability of the polymerization.
The methyl methacrylate(MMA) reversible addition-fragmentation chain transfer(RAFT) miniemulsion polymerization in the presence of β-cyclodextrin(β-CD) was investigated. β-CD is found to act both as an efficient solubilizer for RAFT agent(2-cyanopro-2-yl dithiobenzoate) and as a stabilizer for heterogeneous polymerization. The RAFT miniemulsion polymerizations with or without β-CD were compared in terms of kinetics and the molecular weight distribution. The problem of poor latex stability was observed in this system. A good result of the control over RAFT miniemulsion polymerization of MMA was obtained with β-CD. The increase of the molecular weight of poly(methyl methacrylate) shows a linear relationship with the monomer conversion. The polydispersity index of the polymer with β-CD(PDI=1.18—1.21) is smaller than that without β-CD. TEM photographs showed that the PMMA particles produced with β-CD had smooth surfaces and uniform particle size. Higher amount of sodium dodecyl sulfate and hexadecane was found in favor of improving the controllability of the system. Oil soluble initiator is beneficial to the controllability of the polymerization.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2004年第11期2176-2178,共3页
Chemical Journal of Chinese Universities
基金
国家自然科学基金 (批准号 :2 0 2 760 44 )资助