神头一电厂3号锅炉水冷壁高温腐蚀原因分析及对策 被引量:2

Cause Analysis and Countermeasures of High Temperature Corrosion of No. 3 Boiler' s Water-cooled Wall in Shentou No. 1 Power Plant
下载PDF
导出
摘要 针对锅炉在小修时发现的中间水冷壁高温腐蚀,分析认为内因是燃煤中含硫量较高,外因是高烟温引起水冷壁管壁温度较高和火焰贴壁,壁面存在强还原性气氛。通过进行燃烧调整和设备改进等方面的工作,经过一年的运行考验,未发现新的高温腐蚀。 In light of the high temperature corrosion of intermediate water-cooled wall found out during the minor repair of boiler,it was held thru analysis that,the internal cause was higher sulfur content in fuel coal,while the external cause was higher water-cooled wall temperature resulted from high flue gas temperature and flame closing to wall,and strong reduced atmosphere existed on the wall surface.Through combustion adjustment and equipment improvement etc.works, one year of operation practice showed that no new high temperature corrosion was found.
出处 《电力设备》 2004年第11期64-65,共2页 Electrical Equipment
关键词 锅炉 中间水冷壁 高温腐蚀 分析 对策 boiler intermediate water-cooled wall high temperature corrosion analysis countermeasures
  • 相关文献

参考文献1

  • 1[2]钱述中,彭珂如译.高压汽包锅炉腐蚀的防止.北京:水利电力出版社,1995.

同被引文献13

引证文献2

二级引证文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部