摘要
介绍了不饱和聚酯树脂的粗化工艺流程及各工艺规范。通过正交试验确定了最佳粗化工艺条件:粗化液的体积分数为400mL/L,温度为80～85℃,粗化时间为20min。讨论了粗化液用量、粗化温度和时间对粗化效果和镀层质量的影响。经检测表明,该金属镀层与基体结合力良好。目前该工艺已应用于生产中。
The roughening process of unsaturated polyester resins and its technological criterion were described. The optimal roughening process conditions were identified by orthogonal test as follows: 400 mL/L roughening solution, roughening temperature of 80～85 ℃ and roughening time of 20 min. The influences of roughening solution content, the temperature and roughening time on roughening efficiency and deposit quality were discussed. The results show that the deposits have good adhesion to substrates, and the process has been applied in production.
出处
《电镀与涂饰》
CAS
CSCD
2005年第1期30-31,共2页
Electroplating & Finishing
关键词
不饱和聚酯树脂
非金属电镀
粗化
unsaturated polyester resin
non metal electroplating
roughening