高铁低硅烧结试验研究与实践 被引量:3

Experimental Study and Practice on High Iron and Low Silica Sinter
下载PDF
导出
摘要 通过对太钢高铁低硅烧结技术的试验探讨 ,针对低硅烧结矿所存在的问题 ,提出了改善烧结矿质量的措施以及生产低硅烧结矿的适宜工艺参数 ,为太钢顺利生产和使用低硅烧结矿提供了依据。经过生产实践证明 ,太钢生产碱度为 1.8烧结矿 ,烧结矿的 Si O2 含量降低到 4 %以下 ,会导致烧结矿强度降低 ,粉率升高 ,对高炉炉况顺行不利 ;太钢烧结矿 Si O2 含量控制在 4 .5 %以上 ,铁品位超过了 5 9.7% 。 Through the study of low silica sinter technology,reasonable measures and process parameter were put forward on how to improve the quality of low silica sinter by considering the production difficulty of low silica sinter.The production tests show when the SiO 2 content of sinter less than 4 % and sinter basicity being 1.8,the sinter strength would become deterioration and the blast furnace become difficult to operate.After industrial tests and studies the SiO 2 content of 4.5 % is considered as the reasonable technical index for blast furnaces.
出处 《钢铁》 CAS CSCD 北大核心 2004年第11期10-13,56,共5页 Iron and Steel
关键词 低硅烧结矿 质量 参数 生产实践 low silica sinter, quality, parameters, practice
  • 相关文献

参考文献1

  • 1REN Yunfu .The Effect of Formation and Mineral Composition of Sinter MgO on the Metallurgical Properties.Sinter and Pellet,1984,5(3):1.(任允芙.MgO的赋存状态和矿物组成及其对冶金性能影响的研究.烧结球团,1984,5(3):1.)

同被引文献40

引证文献3

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部