在熔融CaCl2 体系中 ,进行了直接电解还原TiO2 制取钛的实验 ,结果表明 :在电解温度 850℃ ,槽电压 3 .0V下电解数小时可以得到钛。电子探针和X衍射分析表明 :采用 3种不同的TiO2 加料工艺的电解阴极产物含钛量分别达到了 94.646 % ,80 .632 %和 99.784% ,得到的阴极产物呈海绵状或颗粒状。
The new process for electrolysis reduction of TiO_2 to titanium by three different TiO_2 addition means in molten CaCl_2 at 850 ℃ was investigated. The results of EPMA and X-ray analysis indicate that the titanium content of cathodal products are 94.646%, 80.632% and 99.784% respectively. The results show that microstructure of cathodal products are sponge or granule by adding TiO_2 addition means.