铬铁类合金还原脱磷的研究 被引量:5

REDUCING DEPHO5PHORIZATION FOR Fe-Cr,ALLOVS
下载PDF
导出
摘要 在1500℃,用CaSi-CaF_2为脱磷剂对铬铁合金进行了还原脱磷实验,在脱磷剂用量为1/10合金量时,脱磷率近50%。对应于最大的脱磷率存在着一个最佳的初始[C] ̄*,而且随着[Cr]的增加而增加,其定量关系式为[%C] ̄*=1.025+0.055[%Cr];[Cr]和温度对脱磷效果影响不大,这是与氧化脱磷听不同的。还讨论了还原脱磷剂的选择原则和顶渣使用的必要性。最后,结合作者前期氧化脱磷的研究结果,对铬铁类合金的氧化法和还原法脱磷作了综合比较,说明了它们各自的工艺特点和在工业上的应用。 AbstractExperiments on rPdncing depbosphorization for Fe-Cr alloys with CaSi-CaF_2 fluxes were Ca-rried out at 1500℃。Abont 50 % of dephosphorization efficiency was obtainsd when using 10g/100gal-loys of dephosphorizing reagent.Based on the experimental results,the infuenccs of[C] ̄*, [Cr] and temperature on dephosphorization were discussed.It shows that there exists an optimum initial [C] ̄*, corresponding to the maximum dephosphorization efficiency,[C] ̄* is increased with [Cr] and their quantitative relation is[%C] ̄*=1.025+0.055[%Cr].It also shows that [Cr]and temperature almost have no effect on dephosphorization,which are the imporfant featuresdistinguishing from the oxidizing dephosphorization,The princlple of selection of the reagents and the neccessity of using top slag wcre also interpreted.Finally;combining with Our pervious work with regard to oxidizing dephosphorization,oxidizing and reducing methods for Fe-Cr alloys were comprehensively compared, to illustrate their technological characteristics and their industri- al applications respectively.
机构地区 华东冶金学院
出处 《钢铁》 CAS CSCD 北大核心 1994年第12期11-14,10,共5页 Iron and Steel
  • 相关文献

参考文献5

  • 1董元篪,陈友根,刘世洲.CaO-BaO-CaF_2-CaCl_2渣对铬铁系合金的氧化脱磷[J].钢铁研究学报,1994,6(1):15-21. 被引量:7
  • 2董元篪,华东冶金学院学报,1992年,8卷,4期,7页
  • 3朱本立,中国-瑞典冶金科技合作第三阶段共同研究论文集,1992年
  • 4梁连科,钢铁,1991年,26卷,6期,17页
  • 5魏寿昌,钢铁钒钛,1985年,5期,3页

二级参考文献2

共引文献6

同被引文献47

引证文献5

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部