在以前做过的有关工作基础上用 ̄(29)Si-NMR,FT-IR和TMS-GC等方法进一步研究了由水热合成CSH脱水形成β-C_2S的过程。结果表明CSH解聚过程分三步:加热至300℃高聚物解聚主要变成双聚体;300~500℃为双聚体至五聚体;500~1000℃低聚物量降低,而代表β-C_2S的孤立[SiO_4] ̄(4-)四面体量逐步增加成为主要组份。
Based on the previous related study,formation process of C_2S from hydrothermally synthesizedCSH using  ̄(29)Si-NMR,FT-IR and TMS-GC was further studied. The results show that the depolymeriza-tion process of silicate anions in CSH can be divided into three steps: up to 300℃, the high polymers depolymer-ized to dimer mainly,in 300~500℃ the main products formed are dimers together with trimer,tetramer andpentamer;in 500~1000℃,amount of mixture of silicate anions with short chain decreases;whereas amount ofmonomer(SiO_4) ̄(4-) tetrahedra which is symbolic of β-C_2S increases gradually to be the dominant constituent.
出处
《硅酸盐学报》
EI
CAS
CSCD
北大核心
1994年第6期566-572,共7页
Journal of The Chinese Ceramic Society
基金
国家自然科学基金
关键词
水热合成
水化
硅酸钙
活性
硅酸二钙
CSH
C2S
hydrothermally synthesis,calcium silicate hydrate,structure of silicate anions,active dicalcium silicate