高温预析出对7A52合金应力腐蚀性能的影响 被引量:15

Effect of high-temperature pre-precipitation on stress corrosion cracking of 7A52 alloy
下载PDF
导出
摘要 通过对7A52合金时效状态的强度、硬度、电阻率和应力腐蚀性能的测试, 对比分析了高温预析出对7A52合金T4和T61时效状态应力腐蚀和强度性能的影响。结果表明: 高温预析出可以提高 7A52 T4 和 7A52 T61合金的抗应力腐蚀性能, 同时其强度和延伸率有所增加; 高温预析出处理的 7A52 T61 合金拉伸强度达 500MPa, 延伸率13.0%, KISCC达到10.2 MPa·m1/2。 The influence of high-temperature pre-precipitation treatment on tensile property, hardness, electrical resistivities and stress corrosion cracking (SCC) of 7A52-T4 and 7A52-T61 alloys were systematically investigated. The results show that high-temperature pre-precipitation treatment can obviously enhance the resistance to stress corrosion cracking and mildly increase the strength and elongation of 7A52-T61 and 7A52-T4 alloys. After high-temperature pre-precipitation treatment, the tensile strength, elongation and K_(ISCC) of the 7A52-T61 alloys with high-temperature pre-precipitation treatment are 500MPa, 13.0% and 10.2MPa·m^(1/2), respectively.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2005年第3期441-445,共5页 The Chinese Journal of Nonferrous Metals
基金 国家自然科学基金资助项目(50471057) 国家武器装备预先研究资助项目(41312020205)
关键词 Al-Zn—Mg系 铝合金 应力腐蚀 预析出 时效 Al-Zn-Mg series aluminum alloy stress corrosion pre-precipitation ageing
  • 相关文献

参考文献7

二级参考文献43

  • 1宋仁国,曾梅光,张宝金,刘军,金真弘.7050铝合金晶界偏析与应力腐蚀、腐蚀疲劳行为的研究[J].中国腐蚀与防护学报,1996,16(1):1-8. 被引量:37
  • 2[1] HUNSICKER H Y. Rosenhain Centenary Conf, London, UK, September 1975, The Metals Society, 245-262.
  • 3[2] BURLEIGH T D. Postulated mechanisms for stress corrosion cracking of aluminum alloys. A review of the literature 1980-1989,1991,CORROSION 47, (2): 89-98.
  • 4[3] NAJJAR D, MAGMIN T, WARNER T J. Influence of critical surface defects and localized competition between, Mater Sci Eng, 1997,A238: 293-302.
  • 5[4] CINA B. Reducing the susceptibility of alloy, particularly aluminum alloys to stress corrosion cracking, Pat. 3856584,US patent Office, Washington, DC, 24 December 1974.
  • 6[5] PARK J K, ARDELL A J. Effect of retrogression and reaging treatments on the microstructure of Al-7050-T651, Metall Trans. 1984, 15A: 1531-1543.
  • 7[6] OHINISHI T, IBARAKJ Y, ITO T. Improvement of fracture toughness in 7475 aluminum alloy by the RRA process, Mater Trans, JIM, 1989, 8: 601-607
  • 8[7] LUKASAK D A, HART R M. Aluminum alloy development.,Aerosp.Eng, 1991,11:(9),21-24.
  • 9[8] RAJAN K, WALLACE W, BEDDOES J C. Microstructural study of a high-strength stress-corrosion resistant 7075 aluminium alloy., J Mater. Sci, 1982,17. 2817-2825.
  • 10[9] DANH N C, RAJAN K, WALLACE W. A TEM study of microstructural changes during retrogression and reaging in 7075 Aluminum, Metall Trans, 1983, 14A: 1843-1850.

共引文献73

同被引文献167

引证文献15

二级引证文献157

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部