摘要
Based on the tests of a build-up welding at plate edge (BWPE) and amulti-layer build-up welding on plate (MBWP), the article studies on the solid-state phasetransformations which affect welding distortion process and on the influence rule of transformationstarting temperature (TST) of welded metal to the welding residual distortion. The weldingdistortion can be decreased or controlled by the transformation volume expansion caused bysolid-state phase transformation of welded metal during the cooling. The test results of BWPE showthat when TST is at about 190 deg C, the bending distortion of welded specimen is the smallest, andits displacements at free end are decreased to 58 percent and 67 percent compared with those ofconventional welding electrodes A102 and E5015, which TST are less than room temperature and equalto 758 deg C respectively. The test results of MBWP show that when TST were at 100 approx 250 deg C.the welded specimen would appear reversible bending distortion compared with those of A102 andE5015. The maximum deflection value of reversible bending distortion in 8 mm thick plate is -2.94 mmat about 170 deg C of TST. The test results provide a valuable method to decrease or to controlwelding residual distortion.
Based on the tests of a build-up welding at plate edge (BWPE) and amulti-layer build-up welding on plate (MBWP), the article studies on the solid-state phasetransformations which affect welding distortion process and on the influence rule of transformationstarting temperature (TST) of welded metal to the welding residual distortion. The weldingdistortion can be decreased or controlled by the transformation volume expansion caused bysolid-state phase transformation of welded metal during the cooling. The test results of BWPE showthat when TST is at about 190 deg C, the bending distortion of welded specimen is the smallest, andits displacements at free end are decreased to 58 percent and 67 percent compared with those ofconventional welding electrodes A102 and E5015, which TST are less than room temperature and equalto 758 deg C respectively. The test results of MBWP show that when TST were at 100 approx 250 deg C.the welded specimen would appear reversible bending distortion compared with those of A102 andE5015. The maximum deflection value of reversible bending distortion in 8 mm thick plate is -2.94 mmat about 170 deg C of TST. The test results provide a valuable method to decrease or to controlwelding residual distortion.
基金
This project is supported by National Natural Science Foundation of China (No.50175079) China Postdoctoral Science Foundation (No.2003033348).