TEM下自酸蚀粘结剂的两种模式牙本质纳米渗漏观察 被引量:3

Two Models of Nanoleakage Expression in the Self-etching Adhesives
下载PDF
导出
摘要 目的:观察并评价3种自酸蚀粘结剂(ClearfilTM SEBond、AdperTM PromptTM、PANAVIATM F)牙本质粘结界面的纳米渗漏。方法:选取12颗无龋坏人磨牙,用600目碳化硅砂纸在流水冲洗下预备出统一的牙本质粘结面玷污层。分别用3种自酸蚀粘结剂按使用说明进行粘结处理。每颗牙齿垂直于粘结面切割出5个0. 9mm厚粘结试件,分别避光贮存于硝酸银、氨化硝酸银溶液中24h,在TEM下观察牙本质粘结界面纳米渗漏。结果:在TEM下观察到3种自酸蚀粘结剂牙本质粘结界面混合层中呈网状、点状两种模式分布的纳米渗漏。结论:自酸蚀粘结剂由于其自身的组份特性,牙本质粘结界面均存在不同程度的纳米渗漏。 Objective: The purpose of this study was to evaluate the dentin nanoleakage in the 3 self-etching adhesives (Clearfil TM SE Bond, Adper TM Prompt TM , PANAVIA TM F). Methods: Superficial occlusal dentin of 12 molars extracted freshly was finished with 600-grit SiC paper under running water. 3 self-etching adhesives were applied to dentin surfaces according to the manufacturers' instructions. The bonded teeth were sectioned occluso-gingivally into 0.9-mm-thick serial slabs which were stored in silver nitrate group or ammoniacal silver nitrate group in the dark for 24 h and prepared for transmission electron microscope. Rusults: With conventional silver nitrate and ammoniacal silver nitrate, the reticular and spotted pattern modes of nanoleakage were observed within thybrid layers of resin-dentin interfaces bonded with 3 self-etching adhesives under TEM. Conclusion: The nanoleakage expression of resin-dentin interfaces was all observed diversely in the self-etching adhesives because of their properties of composition.
出处 《口腔医学研究》 CAS CSCD 2005年第2期123-126,共4页 Journal of Oral Science Research
基金 国家自然科学基金资助项目 (编号:30371556 /C03031103)
关键词 自酸蚀 纳米渗漏 TEM Self-etching Nanoleakage TEM
  • 相关文献

参考文献8

  • 1Ateyah NZ, Elhejazi AA. Shear bond strengths and microleakage of four types of dentin adhesive materials [J]. J Contemp Dent Pract, 2004, 5(1)∶63-73.
  • 2Deliperi S, Bardwell DN, Papathanasiou A. Effect of different polymerization methods on composite microleakage [J]. Am J Dent, 2003, 16(6)∶73A-76A.
  • 3Sano H, Takatsu T, Ciucchi B, et al. Nanoleakage: leakage within the hybrid layer [J]. Oper Dent, 1995, 20(1)∶18-25.
  • 4Paul SJ, Welter DA, Ghazi M, et al. Nanoleakage at the dentin adhesive interface vs microtensile bond strength [J]. Oper Dent, 1999, 24(3)∶181-188.
  • 5Tay FR, Moulding KM, Pashley DH. Distribution of nanofillers from a simplifyied-step adhesive in acid conditioned dentin [J]. J Adhes Dent, 1999, 23(5)∶103-117.
  • 6Perdigao J, Van Meerbeek B, Lopes MM, et al. The effect of a re-wetting agent on dentin bonding [J]. Dent Mater, 1999, 15(5)∶282-295.
  • 7Li H, Burrow MF, Tyas MJ. Nanoleakage patterns of four dentin bonding systems [J]. Dent Mater, 2000, 16(1)∶48-56.
  • 8Tay FR, King NM, Chan KM, et al. How can nanoleakage occur in self-etching adhesive systems that demineralize and infiltrate simultaneously? [J].J Adhes Dent, 2002, 4(4)∶255-269.

同被引文献149

引证文献3

二级引证文献41

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部