溶析结晶法制备高纯度亚微米硫酸钡粒子 被引量:12

Preparation of Barium Sulfate Submicro-particles with High Purity by Solventing-out Process
下载PDF
导出
摘要 采用溶析结晶法制备亚微米硫酸钡粒子,并运用TEM、SEM、XRD、激光粒度分析仪等分析方法对粒子的粒径、粒度分布、形貌和晶相进行了表征.结果表明溶析结晶法制备的粒子平均粒径160-750nm、粒度分布均匀、纯度高、晶相完整.考察了结晶温度、加料方式、搅拌速率和料液浓度等过程参数以及分散剂对硫酸钡粒子的影响,发现较低的结晶温度, 反向加料方式、较快的搅拌速率、一定的料液浓度等因素有利于制备亚微米硫酸钡粒子. A novel micronization technique using solventing-out crystallization was described for the preparation of submicron BaSO4 particles. The submicron BaSO4 particles were characterized by transmission electron microscope (TEM), scanning electron microscope (SEM), laser diffraction-based particle size analyzer and X-ray diffraction (XRD). The product was obtained as spherical particles with mean sizes from 160 similar to 750 nm. The effects of feed mode, feed concentration, feed rate, agitation intensity and crystallization temperature in the solventing-out process were investigated. A well-efficiency dispersant was selected. The experimental results indicate that lower crystallization temperature, reversed feed mode, higher feed rate, controlling solution concentration to a certain extent and faster agitation rate will lead to producing smaller BaSO4 particles. Furthermore, the purity of submicron BaSO4 particles prepared by solventing-out crystallization is upon to 99.7%, and it indicates that the solventing-out crystallization is not only a micronization technique but also an excellent purification process.
出处 《无机材料学报》 SCIE EI CAS CSCD 北大核心 2005年第4期801-807,共7页 Journal of Inorganic Materials
关键词 硫酸钡 溶析结晶 亚微米 晶相 barium sulfate solventing-out submicro-particles crystalline
  • 相关文献

参考文献14

  • 1Mineral Commodity Summaries, U.S. Geological Survey, January 2004.
  • 2顾薇娜.重晶石产销现状及前景展望[J].中国非金属矿工业导刊,1998(5):38-39. 被引量:3
  • 3.矿产资源综合利用手册[M].科学出版社,2000.521.
  • 4Wang K, Wu J S, Zeng H M. European Polymer Journal, 2003, 39: 1647-1652.
  • 5Boden D P. Journal of Power Sources, 1998, 73: 89-92.
  • 6Chen G G, Luo G S, Xu J H, et al. Powder Technology, 2004, 139: 180-185.
  • 7Ginebra M P, Aparicio C, Albuixech L, et al. Journal of Materials Science: Materials in Medicine, 1999, 10:733-737.
  • 8Ivanova N I, Rudelev D S, Summ B D, et al. Colloid Journal, 2001, 63(6): 714-717.
  • 9Take E, Yekeler M, Ulusoy U, et al. International Journal of Mineral Processing, 2002, 67: 29-42.
  • 10Jones F, Oliveira A, Rohl A L, et al. Journal of Crystal Growth, 2002, 237-239: 424-429.

共引文献3

同被引文献115

引证文献12

二级引证文献53

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部