Investigated the effect of an addition of CaF2 on the crystallization of a glass-ceramic with abrasion resistance. X-ray diffraction, differential thermal analysis and scanning electron microscopy were used to determine the effect. The results showed that a suitable addition of CaF2 promoted crystallization by forming an interme- diate crystalline phase. CaF2 can decrease the temperature and active energy of the base-glass for crystallization. When 4 mass-% of CaF2-fraction is added in the glass, the crystallization temperature and active energy is 936 ℃and 172.75 kJ/mol respectively. When CaF2 is increased to 6 mass-%, the temperature and active energy decrease to 890 ℃ and 88.81 kJ/mol. CaF2 is an efficient nucleating agent for the glass-ceramics with abrasion resistant, the optimal content of CaF2 is about 6 mass-%.
Investigated the effect of an addition of CaF2 on the crystallization of a glass-ceramic with abrasion resistance. X-ray diffraction, differential thermal analysis and scanning electron microscopy were used to determine the effect. The results showed that a suitable addition of CaF2 promoted crystallization by forming an interme- diate crystalline phase. CaF2 can decrease the temperature and active energy of the base-glass for crystallization. When 4 mass-% of CaF2-fraction is added in the glass, the crystallization temperature and active energy is 936 ℃and 172.75 kJ/mol respectively. When CaF2 is increased to 6 mass-%, the temperature and active energy decrease to 890 ℃ and 88.81 kJ/mol. CaF2 is an efficient nucleating agent for the glass-ceramics with abrasion resistant, the optimal content of CaF2 is about 6 mass-%.
基金
Supported by National Natural Science Foundation of China and Shanghai Baosteel Group Corporation(50174024)