PVA复合磷酸钙骨水泥的制备和性能研究 被引量:4

Preparation and property of calcium phosphate bone cement containing PVA
下载PDF
导出
摘要 将含有不同质量分数聚乙烯醇(PVA)的PVA-KH2PO4-Na2HPO4体系缓冲溶液作为骨水泥的调和液,将其与磷酸钙骨水泥粉末混合后成型。将试样在接近生理条件(相对湿度100%,温度(37±1)℃)下养护24h,发现PVA掺入量为1%时的抗压强度达到31.71MPa,比未掺入的提高了将近70%。 PVA of various mass were added into the solution to formulate mixed solution of various mass percent, Compressive strength of the resulted samples which were added 1% PVA was 31.71 MPa after ageing in nearly physiological conditions (100% relativehumidity, (37±1)°C), and it is the best. It could have been improved by 70% compared with the samples without PVA.
出处 《功能材料》 EI CAS CSCD 北大核心 2005年第7期1062-1064,1068,共4页 Journal of Functional Materials
基金 江苏省教育厅研究生创新计划基金资助项目(2001CB610703)
关键词 生物材料 骨水泥 聚乙烯醇 Biomaterials Cements Compressive strength Energy dispersive spectroscopy Orthopedics Polyvinyl alcohols Repair Scanning electron microscopy X ray diffraction analysis
  • 相关文献

参考文献5

二级参考文献8

  • 1唐膺,翁文剑,陆剑平.热压烧结羟基磷灰石生物陶瓷[J].中国陶瓷,1994,30(2):4-7. 被引量:5
  • 2刘昌胜,沈卫,顾燕芳,胡黎明.非陶瓷羟基磷灰石人工骨的研究[J].化工进展,1996,15(1):10-14. 被引量:10
  • 3刘昌胜.新型骨修复材料——磷酸钙骨水泥的制备及其应用基础研究[博士学位论文].上海:华东理工大学,1996..
  • 4Liu C S,J Mater Sci Mater Med,1997年,8卷,12期,803页
  • 5刘昌胜,博士学位论文,1996年
  • 6Gu P,Cem Concr Res,1993年,23卷,3期,531页
  • 7Xie P,Cem Concr Res,1993年,23卷,2期,359页
  • 8Xu Z,Cem Concr Res,1993年,23卷,4期,853页

共引文献30

同被引文献58

  • 1戴红莲,李世普,贺建华,闫玉华.碳纤维增强α-TCP/TTCP骨水泥的研究[J].无机材料学报,2004,19(5):1025-1030. 被引量:19
  • 2马立新,杨南如.聚合磷酸钙骨水泥的物性研究[J].硅酸盐通报,2005,24(2):42-44. 被引量:1
  • 3赵萍,孙康宁.纤维增强磷酸钙骨水泥生物复合材料初探[J].生物骨科材料与临床研究,2004,1(3):14-16. 被引量:12
  • 4马立新,杨南如.自硬化磷酸钙骨水泥的微结构分析[J].硅酸盐通报,2005,24(3):3-5. 被引量:1
  • 5刘忠国,刘一,刘昌胜,付长峰.CPC提高椎体钉固定强度的体外实验研究[J].中国骨与关节损伤杂志,2005,20(9):614-616. 被引量:7
  • 6Wang X H,Ma J B,Feng Q L,Cui FZ.Skeletal repair in rabbits with calcium phosphate cements incorporated phosphorylated chitin.Biomaterials,2002,23:4591-4600
  • 7Wang X,Ma J,Feng Q L,et al.In Vivo Evaluation of S-Chitosan Enhanced Calcium Phosphate Cements.Journal of Bioactive & Compatible.Polymers,2003,6 (18):259-265
  • 8Yokoyama Atsuro,Yamamoto Satoru,Kawasaki Takao,et al.Development of calcium phosphate cement using chitosan and citric acid for bone substitute materials.Biomaterials,2003,23(4):1091-1101
  • 9Kurashina K,Kurita H,kotani A,et al.Experimental cranioplasty and skeletal augmentation using an α -tricalcium phosphate/dicalcium phosphate dibasic/tetracalcium phosphate monoxide cement:a preliminary short-term experiment in rabbits.Biomaterials.1998,19:701-706
  • 10Xu H H,Quinn J B.Calcium phosphate cement containing resorbable fibers for short-term reinforcement and macroporosity.Biomaterials,2002,23:193-202

引证文献4

二级引证文献28

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部