定向凝固钴基高温合金中碳化物形态和分布 被引量:9

MORPHOLOGY AND DISTRIBUTION OF CARBIDES IN DIRECTIONALLY SOLIDIFIED COBALT BASE SUPERALLOY
下载PDF
导出
摘要 本文研究一种定向凝固钴基高温合金中碳化物的形态和分布,结果表明,随凝固速度(ν)的增大,碳化物含量存在一极大值,ν<7mm/min时,碳化物量随ν增加,ν>7mm/min时,则反之,碳化物的尺寸则呈直线趋势下降。随距水冷板距离增大,碳化物量和尺寸均单调增加。碳化物量和尺寸随凝固参数的变化规律是合金性能变化的内在本质因素。 The morphology and distribution of carbides in a directionally solidified cobalt-base superalloy have been studied. When the silidification rate,ν, was 7 mm/min the alloy contatined a maximum content of carbides. The carbide content increases as the increasing in ν up to 7 mm/min, and then, it decreases with the increase in νover 7mm/min, and the size of carbides reduces sharply. Both content and size of carbides increase nomotonously with the distance apart from the chilled plate.
出处 《金属学报》 SCIE EI CAS CSCD 北大核心 1995年第12期A543-A548,共6页 Acta Metallurgica Sinica
关键词 定向凝固 碳化物 相变 钴基合金 耐热合金 directional solidification, Co base superalloy, carbide, phase transformation
  • 相关文献

参考文献2

  • 1Wang H M,Acta Met Sin,1992年,5卷,1期,66页
  • 2姚向东

同被引文献36

引证文献9

二级引证文献18

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部