微封装法制备空心塑料微球 被引量:16

THE FABRICATION OF HOLLOW PLASTIC MICROSPHERES BY MICROENCAPSULATION METHOD
下载PDF
导出
摘要 采用微封装法,以聚苯乙烯(PS)为成球物质,对成球的乳化搅拌速度、溶液浓度、水/有机相体积比、实验温度及真空度等因素进行了研究。在此基础上,成功地制得了单壳PS空心微球。其几何参数为:直径100~300μm、壁厚2~8μm、球形度≥95%、同心度≥90%、表面粗糙度≤300nm。 AbstractIn inertial-confinement fusion (ICF)researches,low-Zplastic microspheres used asfuel containers can provide more efficient ablative implosion and significantly reduceradiation preheat compared with the glass shells.The fabrication of plastic microspheres bymicroencapsulation method consists of three main stages which are described using thefollowing emulsion terminology:(W)defines the aqueous phase,(O)defines the organicphase. The W/O emulsion is first formed by adding water containing a small quantity of thesurfactant to a rappidly stirred organic solution. The W/O emulsion is then added to a largevolume of water also containing surfactant and by further stirring a(W/O)/W dispersionis formed consisting of water droplets encapsulated in a thin layer of polymeric solutionsuspended in water.By evaporating the solvent of organic phase,the plastic microsphereswhich encapsulate water in them are formed.After filtered the plastic microspheres aredried at a lower temperature to remove the interior water.Finally the hollow plasticmicrospheres are formed. Polystyrene (PS)was used as the material for the fabrication of microspheres.The mainparameters of microencapsulation method having influence on the size and quality ofmicrospheres,such as the emulsifying rotating speed,the concentration of solution,thevolume ratio of water/organic phases,the temperature and vacuum of operation werestudied.And PS microspheres with diameter from l00 to 300μm,wall thickness of 2 to 8μmwere produced.The microspheres concentricity,sphericity and surface roughnesses aretypically less than 5%, 10% and 300nm respectively.The microspheres are suitable for thefuel container of ICF targets.
出处 《强激光与粒子束》 EI CAS CSCD 1995年第1期151-156,共6页 High Power Laser and Particle Beams
基金 中国工程物理研究院国防科委预研基金
  • 相关文献

同被引文献102

引证文献16

二级引证文献59

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部