环氧化天然橡胶与聚丙烯共混的研究 被引量:3

Study on Blend of ENR and Polypropylene
下载PDF
导出
摘要 对环氧化天然橡胶ENR-50与聚丙烯共混制备热塑性弹性体进行了研究。试验结果表明,选用硫黄给予体硫化体系、采用“母炼胶”二段混炼工艺,加入适量的相容剂及白炭黑,可制得力学性能较好(拉伸强度15MPa、扯断伸长率500%、撕裂强度83kN·m-1)、中等耐油的热塑性弹性体。透射电镜观察表明,加入相容剂及白炭黑能有效地改善共混物的界面状况,从而提高共混物的力学性能。 A study was made on the TPE prepared with ENR-50/polypropylene blend.The test results showed that a TPE with good physical properties (tensile strength 15MPa,elongation at break 500%, tear strength 84kN. m-1 ) and moderate oil resistance could be made using two stage mixing process,sulfur donor system,and adequate compatibilizer and silica. It was observed with TEM that the boundary condition could be improved effectively with the addition of compatibilizer and silica, thus the physical properties of the blend improved.
机构地区 华南理工大学
出处 《橡胶工业》 CAS 北大核心 1995年第4期202-206,共5页 China Rubber Industry
关键词 环氧化 天然橡胶 聚丙烯 共混 热塑性弹性体 ENR, polypropylene, blend, TPE
  • 相关文献

参考文献1

  • 1邓本诚.共混型热塑性弹性体的新进展[J]合成橡胶工业,1988(02).

同被引文献62

引证文献3

二级引证文献30

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部