摘要
The effects of acid-soluble Al content on the physical and chemical performances of high Al steels were investigated. The results show that the distribution of acid-soluble Al in steel substrate is uniform. With increasing Al content, the strength and toughness of steels decrease a little but the hardness increases. The average yield strength and tensile strength are 425MPa and 570MPa, respectively, and the Rockwell hardness is 89.7. For non-Al steels the average oxidation rate is up to 0.421mg/(cm2·h) at 1373K. For high Al steels, when the mass fraction of Al is less than 5%, there is a thinner gray oxidized layer on surface and the oxidation rate is high; when the mass fraction of Al is more than 8.0%, the thin, close and yellow glossing film still exists, and the average oxidation rate is only 0.016mg/(cm2·h).
The effects of acid-soluble Al content on the physical and chemical performances of high Al steels were investigated. The results show that the distribution of acid-soluble Al in steel substrate is uniform. With increasing Al content, the strength and toughness of steels decrease a little but the hardness increases. The average yield strength and tensile strength are 425 MPa and 570 MPa, respectively, and the Rockwell hardness is 89.7. For non-Al steels the average oxidation rate is up to 0. 421 mg/（cm^2·h） at 1373 K. For high Al steels, when the mass fraction of Al is less than 5%, there is a thinner gray oxidized layer on surface and the oxidation rate is high; when the mass fraction of Al is more than 8.0%, the thin, close and yellow glossing film still exists, and the average oxidation rate is only 0.016 mg/（cm^2·h）.
基金
Project(200202)supportedbytheScienceandTechnologyFoundationforExcellentYouthofAnhuiProvince
project(2003kj077)supportedbytheEducationOfficeofAnhuiProvince