铝酸盐及添加剂对铝阳极电化学性能的影响 被引量:3

Effects of NaAlO_2 and Additives on Electrochemical Behavior of Aluminum in Alkaline Solution
下载PDF
导出
摘要 为了扩大铝阳极的应用范围,采用添加剂来降低其腐蚀速度,同时活化铝阳极。用塔菲尔曲线、线性扫描伏安法、恒电流放电等方法,研究了在4mol/LKOH溶液中,NaAlO2及添加剂NaF对铝(99.999%)阳极电化学性能的影响。结果表明:NaAlO2对铝阳极有害,NaAlO2的浓度不要超过3mol/L;但添加50mmol/LNaF在3.5mol/LNaAlO2+4mol/LKOH中,则铝的腐蚀电流密度由23.7mA/cm2降低到20.8mA/cm2,电极电位由-0.75V负移到-1.50V,开路电位由-1.64V负移到-1.68V,电位滞后时间缩短,基本上恢复到铝在4mol/LKOH溶液中的电化学性能。 With a view to the decreasing of the corrosion rate and activation of aluminum anode by some additives, the effects of NaAlO_2 and additive NaF on the electrochemical properties of aluminum ( 99.999%) anode in a 4 mol/L KOH solution were studied using Tafel curves, linear scanning voltammetry and constant current discharge curves. The results indicated that NaAlO_2 was harmful to the aluminum anode, and it could be imperative to keep the concentration of NaAlO_2 below 3.0 mol/L. When NaF was added into the mixed solution of 3.5 mmol/L NaAlO_2 plus 4 mmol/L KOH at a concentration of 50 mmol/L, the corrosion current density (J_ corr) of the aluminum decreased from 23.7 mA/cm~ 2 to 20.8 mA/cm~ 2, the electrode potential shifted from -0.75 V to -1.50 V, the open circuit potential E_ ocp shifted from -1.64 V to -1.68 V, and the potential lag time decreased as well. This was essentially the same as those for the aluminum in 4 mol/L KOH solution, indicating that the additive NaF was capable of retaining the electrochemical properties of the Al alloy in the NaAlO_2 solution of a quite high concentration.
出处 《材料保护》 CAS CSCD 北大核心 2005年第9期15-17,共3页 Materials Protection
关键词 电化学性能 铝阳极 添加剂 electrochemical properties aluminum anode additive
  • 相关文献

参考文献3

二级参考文献12

  • 1王盛水(译),无机化学原理,1988年,149页
  • 2曹楚南,腐蚀电化学原理,1985年,159页
  • 3齐公台,中国海上油气.工程,1997年,9卷,5期
  • 4GB4948 85铝 锌 铟系合金牺牲阳极,1985年
  • 5《稀土》编写组,稀土,1978年
  • 6毕毕柯夫H H,海船电化学保护,1975年
  • 7Li Qingfeng, Bjerrum Niels J. Aluminum as anode for energy storage and conversion: a review [J].J.Power Sources, 2002, 110:1~10.
  • 8Shao Hai-bo, Wang Jian-ming, Zhang Zhao, et al. Electrochemical impedance spectroscopy analysis on the electrochemical dissolution of aluminum in an alkaline solution [J].J. Electroanalytical Chemistry, 2003, 549: 145~150.
  • 9Shao Hai-bo, Wang Jian-ming, Zhang Zhao, et al. The inhibition effect of calcium tartrate on the corrosion of pure aluminum in an alkaline solution.[J]. Corrosion, 2001, 57(7): 577~581.
  • 10Shao Hai-bo, Wang Jian-ming, Zhang Zhao, et al. The cooperative effect of calcium ions and tartrate ions on the corrosion inhibition of pure aluminum in an alkaline solution[J]. Mater. Chem. Phys., 2003, 77(2): 305~309.

共引文献24

同被引文献10

引证文献3

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部