The growing process of a hydrogen blister in a wheel steel was observed in situ with an optical microscope, and the fracture surfaces formed from broken blisters on a wheel steel and bulk metallic glass were investigated. The initiating, growing, cracking and breaking of hydrogen blis-ters are as follows. Supersaturated vacancies can increase greatly during charging and gather together into a vacancy cluster (small cavity). Hydrogen atoms become hydrogen molecules in the vacancy cluster and hydrogen molecules can stabilize the vacancy cluster. The small cavity becomes the nucleus of hydrogen blister. The blister will grow with enter-ing of vacancies and hydrogen atoms. With increasing hy-drogen pressure, plastic deformation occurs first, the hydro-gen blister near the surface extrudes, and then cracks initiate along the wall of the blister with further increasing hydrogen pressure. A cracked blister can grow further through propa-gating of cracks until it breaks.
The growing process of a hydrogen blister in a wheel steel was observed in situ with an optical microscope, and the fracture surfaces formed from broken blisters on a wheel steel and bulk metallic glass were investigated. The initiating, growing, cracking and breaking of hydrogen blisters are as follows. Supersaturated vacancies can increase greatly during charging and gather together into a vacancy cluster （small cavity）. Hydrogen atoms become hydrogen molecules in the vacancy cluster and hydrogen molecules can stabilize the vacancy cluster. The small cavity becomes the nucleus of hydrogen blister. The blister will grow with entering of vacancies and hydrogen atoms. With increasing hydrogen pressure, plastic deformation occurs first, the hydrogen blister near the surface extrudes, and then cracks initiate along the wall of the blister with further increasing hydrogen pressure. A cracked blister can grow further through propagating of cracks until it breaks.
基金
This work was supported by the National Natural Science Foundation of China(Grant No.50471096).