In this paper,the nanometer TiO2-SiO2 composite oxide,which has a higher surface area,was prepared by sol-gel.The surface area and structural property of composite oxide were examined.The results indicated that nanometer particles of the composite oxide were obtained.When nSi∶nTi ratio was equal to 4.6,the surface area was larger comparing with pure TiO2 and pure SiO2.Tris(2,2’-bipyridine) ruthenium(Ⅱ) absorbed on TiO2-SiO2 composite oxide was sensitive to oxygen.
In this paper, the nanometer TiO2 - SiO2 composite oxide, which has a higher surface area,was prepared by sol - gel. The surface area and structural property of composite oxide were examined. The results indicated that nanometer particles of the compos- ite oxide were obtained. When nsi: nTi ratio was equal to 4.6 ,the surface area was larger comparing with pure TiO2 and pure SiO2. Tris(2,2'- bipyridine) ruthenium( Ⅱ ) absorbed on TiO2 -SiO2 composite oxide was sensitive to oxygen.
出处
《化学研究与应用》
CAS
CSCD
北大核心
2005年第6期808-810,共3页
Chemical Research and Application
关键词
TiO2-SiO2复合氧化物
联吡啶钌
氧敏感性
TiO2 - SiO2 composite oxide
Tris(2,2 - bipyridine) ruthenium( Ⅱ ) [ Ru( bpy)3^2+ ]
oxygen - sensing