The feasibility of photocatalytic degradation of the formaldehyde gas by titanium dioxide （TiO2）/polyester non-woven fabrics was studied. Tbe effects of parameters such as tbe concentration of TiO2 solution, pH value, and drying temperature on the photocatalytic degradation of the formaldehyde gas were also studied. The results showed that the photodegradation efficiency of the formaldehyde gas increased rapidly with the increasing of the concentration of TiO2 solution up to 15g/L, but when the concentration was in excess of 15g/L, the photodegradation efficiency decreased gradually and fluctuated due to light obstruction and disperse state of TiO2. Adjusting the pH value in the solution, the efficiency of photocatalytic degradation of the formaldehyde gas could be improved. The mechanisms of the reaction and the role of the additives were also investigated. After 42hours, TiO2/ polyester non-woven fabric showed no significant loss of the photocatalytic activity.
The feasibility of photocatalytic degradation of the formaldehyde gas by titanium dioxide （TiO2）/polyester non-woven fabrics was studied. The effects of parameters such as the concentration of TiO2 solution, pH value, and drying temperature on the photocatalytic degradation of the formaldehyde gas were also studied. The results showed that the photodegradation efficiency of the formaldehyde gas increased rapidly with the increasing of the concentration of TiO2 solution up to 15g/L, but when the concentration was in excess of 15 g/L, the photodegradation efficiency decreased gradually and fluctuated due to light obstruction and disperse state of TiO2. Adjusting the pH value in the solution, the efficiency of photocatalytic degradation of the formaldehyde gas could be improved. The mechanisms of the reaction and the role of the additives were also investigated. After 42hours, TiO2/polyester non-woven fabric showed no significant loss of the photocatalytic activity.
基金
ThisresearchissupportedbyNationalNaturalScienceFoundationofChina(No.50343020)