恢复加热温度对疲劳损伤后累积寿命的影响

Effect of Heating Temperature for Recovering Fatigue Damage on Accumulated Life
下载PDF
导出
摘要 通过试验研究了恢复加热温度对45钢疲劳损伤后累积疲劳寿命的影响。结果表明:疲劳损伤后在不同的温度下加热时析出碳化物的尺寸、数量不同,亚结构不同,累积疲劳寿命也不同。600℃时析出的碳化物颗粒数量最多且弥散分布,累积疲劳寿命最高。 The effect of heating temperature for recovering fatigue damage on accumulated fatigue life of 45 carbon steel has been investigated. The size and numbers of precipitated carbide particles and the steady sub-grain structure were different after heating 45 carbon steel damaged by fatigue at various temperatures. The lives of accumulated fatigue were also different. The recovery heating at 600 ℃ may reach the best effect. The number of carbide particles was the largest and the particles were distributed in a uniform and dispersed way. And then, the accumulated fatigue life was the longest.
出处 《机械工程材料》 CAS CSCD 北大核心 2005年第12期10-12,16,共4页 Materials For Mechanical Engineering
关键词 45钢 疲劳损伤 恢复加热 疲劳寿命 45 carbon steel fatigue damage recovery heating fatigue life
  • 相关文献

参考文献5

二级参考文献10

  • 1曹起骧,韩静涛,马庆贤,郑涛,谢云岫,李福利.大型管板锻件夹杂性裂纹形成机理探讨[J].塑性工程学报,1994,1(1):14-19. 被引量:16
  • 2金宁,博士学位论文,1990年
  • 3曲敬信,钢铁研究学报,1992年,4卷,2期,47页
  • 4栾道成,博士学位论文,1991年
  • 5孙尧卿,汽车工艺与材料,1989年,6期,28页
  • 6陈南平,机械零件失效分析,1988年
  • 7姚启均,金属机械性能试验常用数据手册,1985年
  • 8刘才穆,金属的疲劳与断裂(译),1983年
  • 9颜鸣皋,断裂物理与断裂力学学术讨论会文集,1978年
  • 10曲敬信,栾道成,杨东方,邵荷生.新型高强韧性奥—贝组织低合金钢的研究[J].中国矿业大学学报,1992,21(4):20-25. 被引量:5

共引文献44

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部