含CL-20 NEPE推进剂的力学性能 被引量:14

Mechanical Properties of NEPE Propellant Containing CL-20
下载PDF
导出
摘要 采用光电子能谱(XPS)和显微红外光谱(M IR)研究了4种键合剂(M APO,22#,HX-752,T 313)与CL-20的相互作用。结果表明,键合剂可以作为CL-20的包覆剂;由于海因和三聚异氰酸酯键合剂(22#)的环状结构以及具有较多的极性基团,对CL-20的包覆性最好。含CL-20的NEPE推进剂力学性能测试结果表明,22#键合剂对提高含CL-20的NEPE推进剂体系的力学性能非常有利,其拉伸强度和断裂延伸率均有较大的提高,分别增加了18.8%和103.4%。 The interaction between four bonding agents and CL-20 was investigated by means of XPS and MIR. The analysis proves that bonding agents can act as the liner of CL-20 and a bonding agent containing hydantoin and tripolyisocynate, which is defined as 22^# , is the best liner of CL-20 owing to its cyclic structure and polar groups. The mechanical properties of NEPE propellant containing CI.-20 with 22^# as bonding agent were studied by tensile test. The test results show that the mechanical properties of NEPE propellant are improved and the tensile strength and elongation-to-break are improved by about 18.8% and 103.4% respectively owing to the addition of CL-20. And the tensile strength of propellant increase with the increasing of the content of PET with three functional groups (f=3) as bonding agent.
出处 《火炸药学报》 EI CAS CSCD 2005年第4期28-31,共4页 Chinese Journal of Explosives & Propellants
关键词 物理化学 CL-20 NEPE推进剂 键合剂 力学性能 physical chemistry hexanitrohexaazaisowurtzitane (CL-20) NEPE propellant bonding agent mechanical property
  • 相关文献

参考文献3

二级参考文献6

共引文献54

同被引文献121

引证文献14

二级引证文献106

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部