摘要
在微波辐射下用变速滴加共沉淀法合成了粒径为10 nm^40 nm的Mg-A l纳米水滑石(nano-HT),其结构经XRD,TEM,TG和元素分析表征。以nano-HT为载体,制备了Cu/nano-HT和CuN i/nano-HT催化剂,通过苯酚羟基化反应考察了它们的催化活性,实验结果表明,双氧水有效利用率和产物的选择性均比以常规水滑石为载体的催化剂高。
Nano-hydrotalcite（nano-HT, 10 nm - 40 nm） was synthesized by the method of variablespeed dripping alkali under microwave irradiation and was characterized by XRD, TEM, TG and elemental analysis. The catalysts of Cu/nano-HT and CuNi/nano-HT were prepared using nano-HT as a supporter. The catalytic activities of the catalysts were studied in phenol hydroxylation. The results showed that the effective utilization-ratio of hydrogen peroxide and the selectivity of reaction were better than the conventional hydrotalcites.