45钢等径弯曲通道变形及组织细化研究 被引量:5

Study of ECAP Distortion and Structure Refinement for No.45 Steel
下载PDF
导出
摘要 研究了等径弯曲通道(ECAP)变形后45钢中先共析铁素体及珠光体组织的演变特征。结果表明,ECAP变形4道次后,片层状的珠光体组织演变成了超细的渗碳体颗粒均匀分布于亚微晶铁素体基体的组织。先共析铁素体由原始的平均晶粒尺寸约为30μm演变为大角度晶界分离的、平均晶粒尺寸约为0.4μm的超细晶组织。ECAP变形后,先共析铁素体首先在其内部会形成具有薄片层界面(LBs)的板条位错胞甚至亚晶组织。进一步变形时位错胞或亚晶可继续细化。再进一步变形时通过晶界滑移和晶粒旋转的方式可以获得具有大角度晶界分离的、等轴的超细晶组织。 The microstructure evolution of proeutectoid ferrite and pearlite in No. 45 Steel after ECAP (equal-channel angular pressing) was investigated. The results show that the mierostrueture of lamellae pearlite has changes to ultra fine cementite particles throughout the ferrite matrix uniformly after four-pass distortion. The proeutectoid ferrite grains of about 30μm change to high-angle boundary ultra-flne grains of about 0.4μm. After ECAP distortion, even dislocations and subgrains with lamellar boundaries (LBs) are formed in inner proeutectoid ferrite grains. With further deformation, the dislocations and subgrains are refined. At the larger strain, equiaxed ultra-fined ferrite grains with high-angle boundaries are formed by grains sliding and rotation.
出处 《钢铁》 CAS CSCD 北大核心 2006年第1期74-79,共6页 Iron and Steel
基金 国家自然科学基金资助项目(59974018) 陕西省自然科学基金资助项目(2003E121)
关键词 ECAP变形 45钢 超细晶 铁素体 珠光体 ECAP deformation No. 45 steel ultra-fine grain ferrite pearlite
  • 相关文献

参考文献9

  • 1Segal V M, Engineering and Commercialization of Equal Channel Angular Extrusion[J], Materials and Engineering A,2004, 386(1-2):269-276.
  • 2Shin D H, Kim B C, Park K-T, et al, Microstructural Changes in Equal-channel Angular Pressed Low Carbon Steel by Static Annealing[J]. Acta Materialia, 2000,48(12): 3245-3252.
  • 3Aoki K, Azushima A. Properties of Uhrafine-grained Steel by Repeated Shear Deformation of Side Extrusion Process[J],Materials Science and Engineering A, 2002, 337 (1-2):45-49.
  • 4Fukuda Y, Oh-Ishi K, Horita Z, et al, Processing of a Low-carbon Steel by Equa channel Angular Pressing [J], Acta Materialia, 2002, 50(6),1359-1368.
  • 5Park K T, Han S Y, Ahn B D, et al. Ultrafine Grained Dual Phase Steel Fabricated by Equal-channel Angular Pressing and Subsequent Imercritical Annealing [J]. Scripts Materialia,2004, 51(9) :909-913.
  • 6Iwahashi Y, Wang J, Horita Z, et al. Principle of Equal-channel Angular Pressing for the Processing of Ultra-flne Grained Materials[J]. Scripta Materialia, 1996, 35(2):143-146.
  • 7Furukawa M, Iwahashi Y, Horita Z, et al. Shearing Characteristics Associated with Equal-channel Angular Pressing[J]. Materials Science and Engineering A, 1998, 257(2):328-332.
  • 8Hughes D A, Hansen N. Microstructure and Strength of Nickel at Large Strains[J]. Aeta Materialla, 2000, 48(11):2985-3004.
  • 9Nakashima K, Horita Z, Nemoto M, et al. Influence of Channel Angle on the Development of Ultrafinc Grains in Equal-channel Angular Pressing[J]. Acta Materialia, 1998,46(5) : 1589-1599.

同被引文献96

引证文献5

二级引证文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部