MoS_2在菜籽油中的高温摩擦磨损性能研究 被引量:5

High Temperature Tribological Behaviors of MoS_2 in Colza Oil
下载PDF
导出
摘要 采用多功能SRV摩擦磨损试验机考察了含质量分数5%MoS2的菜籽油的高温摩擦磨损性能.结果表明:在点接触条件下,MoS2在200-400℃范围内表现出非常低的摩擦系数(约0.06),但在100℃和500℃时,其摩擦系数与菜籽油相当;在线接触条件下,MoS2在不同温度下的摩擦系数变化趋势与点接触条件下的相似;无论在点接触还是线接触条件下,MoS2在不同试验温度下的抗磨性能均比菜籽油好,尤其在300℃时MoS2显示出优异的抗磨性能,含5%MoS2的菜籽油在300℃时显示出非常优异的减摩抗磨性能.这是因为MoS2主要以吸附形式存在于摩擦表面. High temperature tribological behavior of colza oil with 5.0 wt%MoS2 additive has been investigated using SRV multifunctional test system. Chemical states of elements on the worn surface were analyzed using X-ray photoelectron spectroscopy (XPS). Results show that MoS2 exhibited very low friction coefficient (0.06) between 200-400℃ at point contact condition, but it exhibited similar friction coefficient as colza oil did at 100℃ and 500℃. MoS2 exhibited similar tendency of variation of friction coefficient with different temperature in comparison with experiment done at line contact condition. At both point contact and line contact condition, MoS2 exhibited better wear resistance than colza oil at different temperature, especially MoSz exhibited superior performance at 300℃. Colza containing 5.0%MoSz exhibited superior performance of friction reducing and anti-wear property because MoS2 adsorbed on rubbing surface.
出处 《摩擦学学报》 EI CAS CSCD 北大核心 2006年第1期41-44,共4页 Tribology
基金 国家自然科学基金重点项目资助(50235030)
关键词 MOS2 高温 菜籽油 摩擦磨损性能 MoS2, high temperature, colza oil, friction and wear behavior
  • 相关文献

参考文献8

二级参考文献20

  • 1齐尚奎,薛群基,张绪寿,冯良波.二硫化钼表面氧化行为的研究(Ⅱ)─—二硫化钼摩擦表面氧化与电子转移的研究[J].摩擦学学报,1994,14(1):17-24. 被引量:9
  • 2陈建敏,冶银平,党鸿辛.粘结固体润滑膜及其应用[J].摩擦学学报,1994,14(2):180-189. 被引量:56
  • 3廖家轩.[D].Harbin(哈尔滨),.
  • 4[1]Y.Feldman,E.Wasserman,High-rate,gas-phase growth of MoS2 nested inorganic fullerenes and nanotubes[J].Science,1995(267):222-225.
  • 5[2]L.Rapoport,Yu.Billik.Hollow nanoparticles of WS2 as potential solid-state lubricants[J].Nature,1997(387):791-793.
  • 6[3]M.Chhowalla.A.J.Amaratunga.Thin film of fullerene-like MoS2 nanoparticles with ultra-low friction and wear[J].Nature,2000(407):164-167.
  • 7齐尚奎,真空科学与技术学报,1991年,14卷,1期,15页
  • 8桂琳琳,X射线与紫外光电子能谱,1984年
  • 9齐尚奎,Chin Sci Bull,1995年,40卷,4期,300页
  • 10Xiao J(肖军),Zhou H D(周惠娣),Li TH(李铁虎),et al.Protection of ablative adhesion and erosion of slide track of missile launcher by high-temperature two-phase exhaust using MoS2-based bonded solid lubricantfilm(导弹发射

共引文献62

同被引文献68

引证文献5

二级引证文献53

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部