低压脉冲电场下纯铝的晶粒细化 被引量:3

Grain Refinement of Aluminum by Low-voltage Eelectric Current Pulse Discharge
下载PDF
导出
摘要 研究了低压脉冲电场作用下纯铝凝固组织的变化,考察了放电电压和处理时间对纯铝晶粒尺寸的影响。结果表明:低压脉冲电场可以显著地细化纯铝的凝固组织。随着放电电压的提高,纯铝的晶粒尺寸逐渐减小;当放电电压达到400V时,晶粒尺寸略有回弹。随着处理时间的增加,纯铝的晶粒尺寸逐渐减小;当处理时间大于15 min时,纯铝的晶粒尺寸随着处理时间的增加而略有增大。 The influence of low-voltage electric current pulse on solidified microstructure of aluminum was studied, and the effects of discharging voltage and treating time on grain size of aluminum were investigated. The results show that solidified microstructure of aluminum can be refined apparently by low-voltage electric current pulse discharge. The grain size is reduced greatly with the increase of discharging voltage. But when discharging voltage increases further to 400V, the grain size rebounds slightly. As treating time increases from 0 to 15 min, the grain size decreases dramatically and when treating time is more than 15 min, the grain size increases a little.
作者 周全 杨院生
出处 《热加工工艺》 CSCD 北大核心 2006年第1期16-18,共3页 Hot Working Technology
关键词 低压脉冲电场 纯铝 凝同组织 晶粒细化 low-voltage electric current pulse aluminum solidified microstructure grain refinement
  • 相关文献

参考文献8

二级参考文献25

  • 1鄢红春,何冠虎,周本濂,秦荣山,郭敬东,沈以赴.脉冲电流对Sn-Pb合金凝固组织的影响[J].金属学报,1997,33(4):352-358. 被引量:129
  • 2常国威.电渣感应连续定向凝固技术与电流扰动对枝晶间距的影响[M].北京:北京科技大学,1998..
  • 3秦荣山.电脉冲作用下的非平衡转变研究[M].沈阳:中国科学院金属研究所,1996..
  • 4秦荣山,材料研究学报,1995年,9卷,219页
  • 5Li Jianming,Scr Metall Mater,1994年,31卷,1691页
  • 6胡汉起,金属凝固,1985年,301页
  • 7A.K.Misra, Met.Trans. A, 16, 1354(1985)
  • 8A.K.Misra, Met. Trans. A, 17, 358(1986)
  • 9H.Conrad, J.White, W.D.Cao, X.P.Lu, A.F.Sprecher, Material Science and Engineering A, 45, 1(1991)
  • 10W.D.Cao, H.Conrad, Fatigue Fract Engng Mater Struct, 6, 573(1992)

共引文献158

同被引文献46

引证文献3

二级引证文献16

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部