摘要
目的:检测钛铌锆锡(Ti-24Nb-4Zr-7.6Sn)合金铸件的机械性能,评价其作为口腔修复材料的可行性。方法:对钛铌锆锡合金铸件的机械性能、显微硬度进行检测,对剖面组织金相显微结构和断口形貌进行观察。结果:钛铌锆锡合金抗拉强度为681.7 MPa,屈服强度为410 MPa,延伸率为6%,弹性模量为42.1 GPa,维氏硬度为453 Hv;合金金相组织表现为细化的晶粒结构,合金断口呈典型的微孔聚合型断裂形貌。结论:钛铌锆锡合金机械性能能够满足制作口腔修复体的要求。
Objective:To study the mechanical properties of a new titanium alloy with lower elastic modulus for prosthodontic use. Methods:Samples of a newly developed Ti-Nb-Zr-Sn alloy with low elastic modulus were prepared. The microstructure, microhardness profile of the specimen cross section were measured by microhardness test meter and metallurgical microscope. Results:The data of the tensile strength(MPa) ,yield strength(MPa) , elongation ( % ) , elastic modulus (GPa) and microhardness (Hv) of Ti-Nb-Zr-Sn alloy were 681.7,410,6,42.1 and 453 respectively. The microstructure was with fine crystal grains. Conclusion: The microstructure and microhardness profile of the TiNb-Zr-Sn alloy may meet the requirement for dental applications.
出处
《实用口腔医学杂志》
CAS
CSCD
北大核心
2006年第1期57-59,共3页
Journal of Practical Stomatology
基金
国家自然科学基金(30471754号)项目资助