RE-Fe基合金热喷涂层的耐腐蚀性能 被引量:8

Corrosion resistance of RE-Fe alloy thermal spraying coatings
下载PDF
导出
摘要 通过热喷涂的方法制备了添加稀土组分和适量铜组元的RE-Fe基合金涂层。采用液态浸渍法、电化学测试、盐雾实验以及涂层表面腐蚀形貌SEM观察等方法对不同成分、不同喷后处理工艺的RE-Fe基合金涂层的耐腐蚀性能进行研究。结果表明:添加适量的稀土组分和铜组元,使Fe基合金涂层的自腐蚀电位正移,维钝电流密度和致钝电流密度下降,明显地提高了Fe基合金(Fe-Cr-Ni-B-Si)涂层在酸类腐蚀介质中的耐腐蚀性能;同时也有效地提高了涂层抗盐雾气氛腐蚀的能力;其中以添加2%RE氧化物(质量分数)涂层(封孔后)的综合效果最佳。 Through adding different kinds of rare earth(RE) compositions and moderate amount of copper constituent , RE-Fe based alloy coatings were prepared by thermal spraying(THSP). The corrosion resistance of RE-Fe based alloy coatings with different compositions and post-spraying treatments were investigated systematically by maceration corrosion test, electrochemical test, NSS test and scanning electron microscopy. The results show that the addition of moderate amount of rare-earth compositions and copper constituent can increase remarkably the corrosion resistance of iron-based alloy (Fe-Cr-Ni-B-Si) coating in the acid and salt corrosion media, and the coating with 2% RE oxide composition (mass fraction) possesses the best comprehensive effects.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2006年第1期94-99,共6页 The Chinese Journal of Nonferrous Metals
基金 福建省属高等院校测试基金资助项目(980029)
关键词 铁基合金涂层 耐腐蚀性能 热喷涂 稀土 iron-based alloy coating corrosion resistance thermal spraying rare earths
  • 相关文献

参考文献13

二级参考文献47

共引文献265

同被引文献53

引证文献8

二级引证文献14

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部