电热爆炸喷涂WC/Co涂层组织和性能研究 被引量:8

Microstructure and Properties of Electro-thermal Explosion Sprayed WC/Co Coating
下载PDF
导出
摘要 利用电热爆炸喷涂技术,在45钢表面制备了WC/Co耐磨涂层,使用SEM和XRD分析了涂层的组织与相结构,使用显微硬度计和纳米压痕仪测试了涂层的硬度和弹性模量。结果发现,电热爆炸喷涂WC/Co涂层致密,无明显的层状结构;涂层的显微硬度最高达到了2836HV0.1,平均为1704HV0.1;纳米压痕仪测得涂层的弹性模量为346.8 GPa;涂层的相组成主要为WC和W2C;在涂层与基体的结合区,出现柱状晶,证明涂层与基体主要是冶金结合。 The WC/Co coating was prepared on substrate 45 steel with electro-thermal explosion spraying. Microstructure and phase structure of the coating were investigated by SEM, X-ray diffraction, etc. The hardness and elastic modulus were estimated by microhardness meter and nano-indentation instrument respectively. The results show that the WC/Co coating is characterized by compact construction. The average hardness of the coating reachs to 1704HV0. 1 with the highest value of 2836HV0.1. The main phases of the coating are WC and W2C. Columnar crystals appear in the bonded zone between the coating and the substrate and it shows that the bonding between the coating and the substrate is metal lurgical one.
出处 《金属热处理》 EI CAS CSCD 北大核心 2006年第2期23-26,共4页 Heat Treatment of Metals
基金 国家科技部"863"课题(项目编号:2003AA331130)
关键词 电热爆炸喷涂 WC/Co涂层 组织 硬度 electro-thermal explosion spraying WC/Co coatings microstructure hardness
  • 相关文献

参考文献9

  • 1刘宗德,安江英,杨昆,韩铭宝,陆辛.电爆炸高速喷涂新技术研究[J].爆炸与冲击,2001,21(1):17-20. 被引量:38
  • 2Tamura H.Generation of a high-velocity jet in the electrothermal explosion of conductive ceramic powders[J].Journal of Thermal Spray Technolgy,1998,7(1):87-92.
  • 3Tamura H.Zirconium boride and tantalum carbide coatings sprayed by electrothermal explosion of powders[J].Journal of Thermal Spray Technolgy,1997,6(4):463-468.
  • 4刘家俊.材料磨损原理及其耐磨性[M].北京:清华大学出版社,1993..
  • 5Chen H,Hutchings I M.Abrasive wear resistance of plasma-sprayed tungsten carbide-cobalt coatings[J].Surface and Coatings Technology,1998,107:106-114.
  • 6Liao H,Normand B,Coddet C.Influence of coating microstructure on the abrasive wear resistance of WC/Co cermet coatings[J].Surface and Coatings Technology,2000,124:235-242.
  • 7Pharr G M.Measurement of mechanical properties by ultra-low load indentation[J].Materials Science and Engineering A,1998,253(3):151-159.
  • 8Oliver W C,Pharr G M.An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments[J].Journal of Materials Research,1992,7(6):1564-1583.
  • 9Pharr G M,Oliver W C,Brotzen F R.On the generality of the relationship among contact stiffness,contact area and elastic modulus during indentation[J].Journal of Materials Research,1992,7(6):613-617.

二级参考文献5

共引文献47

同被引文献110

引证文献8

二级引证文献67

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部