摘要
介绍了冷轧薄板表面主要缺陷的形貌、形成原因及预防措施。研究表明:冷轧薄板表面缺陷主要分为常规缺陷和非常规缺陷两大类。常规缺陷的产生与冷轧工艺质量密切相关,而非常规缺陷的形成机理则比较复杂,可能在炼钢工序也可能在轧钢工序形成,需具体情况具体分析。
The present paper introduces the appearance, cause of formation of and precautionary measure against the major surface defects of the cold rolled ultra-low carbon steel sheet. Research shows that the surface defects of the cold rolled sheet can be divided into two major categories, i.e. normal defects and abnormal ones. Formation of the normal defects is closely related with the cold rolling process, while the mechanism of formation of the abnormal defects is fairly complicated, very possibly due to either inap- propriate steel-making process or rolling process, and therefore analysis on the specific case is the only way to solve the problem.
出处
《炼钢》
CAS
北大核心
2006年第3期22-25,48,共5页
Steelmaking
关键词
冷轧薄板
常规缺陷
非常规缺陷
cold rolled sheet
normal defect
abnormal defect