柠檬酸、硝酸铵溶液中冷轧钢的腐蚀行为 被引量:4

Corrosion behavior of cold rolled steel in citric acid and NH_4NO_3 solution
原文传递
导出
摘要 利用失重法、动电位极化曲线法研究了室温(20~25℃)下0.01~0.10mol/L柠檬酸、硝酸铵溶液中冷轧钢的腐蚀行为.结果表明,柠檬酸溶液中,冷轧钢的腐蚀速度随柠檬酸浓度的增加而增大,阴、阳两极反应速度也随浓度的增大而加快,但当柠檬酸浓度为0.10mol/L时,阳极反应受到抑制.硝酸铵溶液中。浓度为0.01~0.06mol/L时,钢的腐蚀速度、阴阳两极反应均随浓度的增加而增大;硝酸铵浓度0.06~0.10mol/L时,浓度增加对腐蚀速度和阴极反应影响微弱,而对阳极反应产生抑制作用.详细探讨了腐蚀机理. The corrosion behavior of cold rolled steel in 0.01-0.10 mol/L citric acid and NH4NO3 solution was studied by weight loss and polarization curve methods. The results show that the corrosion rate of cold rolled steel increases with the increase of citric acid concentration. In citric acid solution, both anodic and ca- thodic reactions were accelerated with the increase of acid concentration. However, the anodic reaction was inhibited when the citric acid concentration was 0.10 mol/L. In 0.01-0.06 mol/L NH4NO3 solution, the corrosion rate, anodic reaction and cathodic reaction increased with the increase of acid concentration. In 0.06 0.10 mol/L NH4NO3 solution, both the corrosion rate and cathodic reaction did not change with the increase of acid concentration obviously, while the anodic reaction was inhibited with the increase of acid concenration. The corrosion mechanism was studied.
出处 《云南大学学报(自然科学版)》 CAS CSCD 北大核心 2006年第4期345-349,共5页 Journal of Yunnan University(Natural Sciences Edition)
基金 国家自然科学基金资助项目(50261004) 云南省教育厅青年基金资助项目(03Y150D)
关键词 柠檬酸 硝酸铵 腐蚀 steel citric acid NH4NO3 corrosion
  • 相关文献

参考文献8

二级参考文献29

共引文献196

同被引文献54

引证文献4

二级引证文献12

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部