疏水缔合水溶性聚合物P(AM/NaAA/DiAC_(14))水溶液的黏度行为

Viscosity Behaviors of Aqueous Solution of Water-soluble Hydrophobically Associating Polymers P(AM/NaAA/DiAC_(14))
下载PDF
导出
摘要 采取前加碱二元胶束共聚-共水解法合成了三元疏水缔合水溶性聚合物聚(丙烯酰胺/丙烯酸钠/N,N-双烯丙基十四胺)[P(AM/NaAA/DiAC14)],研究了其水溶液的黏度行为。当x(DiAC14)=0.10%-0.40%时,在30℃、c(NaCl)=1mol·L-1水溶液中,P(AM/NaAA/DiAC14)的特性黏数[η]、黏均相对分子质量Mη^-、Huggins常数KH、平均线团密度ρequ^-分别为18.88—22.22dL·g^-1、9.98×10^6-12.24×10^6g·mol^-1、0.117—0.299和0.112—0.132g·dL^-1;KH小于0.8,表明其分子内缔合作用较弱。P(AM/NaAA/DiAC14)在矿化度为19334μg。盐水溶液中的表观黏度随疏水单体摩尔分数的增加而增加,随温度、剪切速率的增加而降低。在NaCl、CaCl2的离子强度分别为1.26×10^-3-4.88×10^-3mol·kg^-1、1.073×10^-4--5.28×10^-4mol·kg^-1的水溶液中,P(AM/NaAA/DiAC14)出现盐增黏现象,疏水单体摩尔分数越大,盐增黏效应越显著。随疏水单体摩尔分数的增加,临界缔合质量浓度(CAC)降低;与后加的十二烷基硫酸钠(SDS)[ρ(SDS)=0—0.07g·dL^-1]的疏水缔合作用增强,黏度增加的幅度增大。 A series of hydrophobically associating water-soluble polymers poly (acrylamide/sodium acrylate/N, N-diallyl-N-tetradecylamine ) [ P ( AM/NaAA/DiAC14 ) ] were prepared by way of cohydrolysis with alkali before radical micellar copolymerization. Their solution properties were examined. When x ( DiAC14 ) = 0. 1% - 0. 4%, the intrinsic viscosity values [ η ], viscosity average molecular weight of the polymers, Huggins constants Ks and average coil density Pequ were respectively 18.88-22.22dL·g^-1、9.98×10^6-12.24×10^6g·mol^-1、0.117-0.299 and 0.112-0.132g·dL^-1 at 30 ℃ and in c (NaCl) = 1 mol · L^-1 aqueous solution. It was showed that intramolecular hydrophobically associating interactions in the dilute solution were rather weak because Ks were always less than 0.8. In the 19 334μg·g^-1 saline solution, apparent viscosity of the polymers decreased with decrease of hydrophobe mole fraction and with increase in temperature and shear rate. It was observed that there appeared viscosity enhancement in the saline solution of P(AM/NaAA/DiAC14),in which the ionic strength of NaCl and CaCl2 were 1.26×10^-3-4.88×10^-3mol·kg^-1、1.073×10^-4--5.28×10^-4mol·kg^-1 respectively. The more hydrophobe mole fraction, the stronger viscosity enhancement effect. With increase of hydrophobe mole fraction, the critical associating mass concentration (CAC)decreased, and the associative interactions between polymers and sodium dodecyl sulfate ρ(SDS)=0g·dL^-1-0.07g·dL^-1 became stronger.
作者 耿同谋 刘颜
出处 《精细化工》 EI CAS CSCD 北大核心 2006年第8期747-751,共5页 Fine Chemicals
基金 重庆师范大学博士启动基金项目(05×LB010)~~
关键词 疏水缔合 胶束聚合 共水解法 N N-双烯丙基十四胺 黏度行为 hydrophobic association micellar copolymerization co-hydrolysis N, N-diallyl-N- tetradecylamine viscosity behavior
  • 相关文献

参考文献9

  • 1Taylor K C, Nasr-E1-Din H A. Water-soluble hydrophobically associating polymers for improved oil recovery:a literature review[ J]. Journal of Petroleum Science and Engineering, 1998,19:265- 280.
  • 2Candau F, Selb J. Hydrophobically-modified polyacrylamides prepared by micellar polymerization [ J ]. Advances in Colloid and Interface Science, 1999,79 : 149 - 172.
  • 3Volpert E,Selb J,Candau F. Associating behaviour of polyacrylamides hydrophobically rnodilqed with dihexylacrylamide [ J ]. Polymer, 1998,39(5) :1025 - 1033.
  • 4Han D K, Yang C Z, Zhang Z Q, et al. Recent development of enhanced oil recovery in China[ J]. Journal of Petroleum Science and Engineering, 1999,22 : 181 - 188.
  • 5Zhang Y X, Da A H, Butler, et al. A fluorine-containing hydrophobically associating polymer. 1. Synthesis and solution properties of copolymers of acrylamide and fluorine-containing acrylates or methacrylates [ J ]. Journal of Polymer Science : Part A : Polymer Chemistry, 1992,30 : 1383 - 1391.
  • 6张开.高分子物理学[M].北京:化学工业出版社,1996,51.
  • 7Hill A, Candau F, Selb J. Properties of hydrophobically associating polyacrylamides: influence of the method of synthesis [ J ].Macromolecules, 1993,26:4521 - 4532.
  • 8Wei X,Hamley I W,Castelletto V ,et al. Synthesis and characterization of hydrophobically modified polyacrylamides and some observations on theological properties [ J ]. European Polymer Journal,2004,40:47 - 56.
  • 9Ma J,Cui P,Zhao L,et al. Synthesis and solution behavior of hydrophobic association water-soluble polymers containing acylalkyl group [ J ]. European Polymer Journal, 2002,38 : 1627 -1633.

共引文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部